OOA Prepreg B180 CF02 (0/+45° N-S) – High-Temperature Epoxy Carbon Fiber Composite
В180 is a prepreg based on epoxy carbon fiber reinforced resin for producing details with operating temperatures up to 150°C. Out-of-autoclave prepreg technology has the most advantages of autoclave. The autoclave is not required for processing the prepreg B180. Curing takes place in a vacuum bag, with the technology of the package laminating slightly different from the vacuum infusion. It shows the following features and properties:
Properties
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Compressive modulus | 23.0 °C | 60 MPa | ASTM D695, Lamina |
Compressive strength | 23.0 °C | 802 MPa | ASTM D6641, Lamina |
Compressive strength laminate | 25.0 °C | 708 MPa | |
85.0 °C | 639 MPa | ||
Elastic modulus | 23.0 °C | 71 GPa | ASTM D3039, Lamina |
Shear strength, τ₁₂ | 23.0 °C | 126 MPa | |
Tensile strength | 23.0 °C | 871 MPa | ASTM D3039, Lamina |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Marine: The shells of boats and sport catamarans can be made of composites;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite | |
| Processing history | Reinforcing filler: carbon fabric 22502 (twill 2x2, 200 g/m2, HTA40). Carbon plastic is produced by vacuum molding. | |
| Processing methods | Holding at a temperature of 25-30°C, for 12 hours, a vacuum of -1 bar. Heating 2°C/min. up to 120°C, holding at 120°C for 180 minutes. Heating 2°C/min. up to 180°C, holding at 180°C for 180 minutes, cooling no faster than 5°C/min. up to 50°С. | |
Composite material
- Renegade Materials Boosts High‑Heat Carbon‑Fiber Prepreg Capacity 2.5× to Power Advanced Aerospace
- Ensinger Launches Advanced Thermoplastic Prepreg Production Facility in Bavaria
- Kordsa Expands Thermoplastic Prepreg Lineup with New Woven Carbon Sheets
- Advanced Prepreg for Rapid Compression Molding in RAPM
- Notus Composites Reaches 1M sqm of Fire‑Retardant Epoxy Prepreg for Dubai's Museum of the Future
- T107 Epoxy Carbon Fiber Prepreg – High-Temperature, High-Strength Autoclave Material
- T107 Autoclave Epoxy Prepreg (BMI-CF) – High‑Strength, 150°C Operating Temperature
- PSB250 BMI-CF Prepreg – High-Strength Carbon Fiber Resin for 250°C Autoclave Use
- O2A B180 CF08 Prepreg – 0/+45/-45/90° Carbon Fiber Laminate
- OOA Prepreg B180 CF08 [0°/+45°] – High-Performance Epoxy Carbon Fiber for High-Temp Applications