Phenolic RT630S Tube: Superior Machining Grade with Exceptional Electrical & Moisture Resistance
Being a hot oil treated version of RT630, RT630S is a fine machining grade with excellent electrical properties and moisture resistance. It has good dimensional stability and resists splitting.
Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Density | 1.28 g/cm³ | ASTM D792 | |
Moisture absorption | 0.7 % | ASTM D570 | Condition D₁-24/23 |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Compressive modulus | 3.0 GPa | ASTM D695 | Condition A |
Compressive strength | 158.6 MPa | ASTM D695 | Condition A |
Hardness, Rockwell M | 110 [-] | ASTM D785 | |
Tensile strength | 89.6 MPa | ASTM D638 | Condition A |
Thermal
| Property | Value | Comment | |
|---|---|---|---|
Relative temperature index, electrical | 140 °C | ¹ | |
Relative temperature index, mechanical strength | 130 °C | ¹ | |
Flammability | UL Bulletin 94, Class HB, Condition A | ||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Breakdown voltage | 23 kV | ASTM D149 | Condition D48/50 |
80 kV | ASTM D149 | Condition A | |
Dielectric strength | 14.96 kV/mm | ASTM D149 | Condition D-48/50 |
17.71 kV/mm | ASTM D149 | Condition A |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include fuse tubes, coil forms and supports. | |
| Fillers | Paper | |
| Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use 2.The mechanical properties are converted from American unit system to International unit system. | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |
Composite material
- Phenolic RT315 Tube Fabric – High-Performance Medium Weave Cotton with Graphitic Lubricant
- RT370 Phenolic Composite Tube – Superior Strength & Durability
- BT13NPG Phenolic Tube – Medium Weave Cotton Fabric with Graphitic Carbon Lubricant
- High-Performance Phenolic BT18NPM Tube – Superior Strength & Durability
- BT45NPM Phenolic Tube – High-Strength Hybrid Aramid Material
- RT342H Phenolic Tube – Advanced Heat‑Treated Fabric for Superior Machining
- BT13HPN Phenolic Composite Tube – High Strength & Durability
- BT13NPN Phenolic Resin Tube – Durable Medium‑Weight Canvas Construction
- Phenolic BT13SPN Tube – Durable Hot‑Oil Treated Medium‑Weight Canvas Fabric
- Phenolic RT630H Tube – Heat‑Treated Phenolic with Superior Electrical and Moisture Resistance