Premium Hot-Rolled JIS H4000 3203 Aluminium – Superior Strength & Reliability
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.72 - 2.73 g/cm³ | Typical for Wrought 3000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.5 - 70.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Elongation | 8.0 % | hot-rolled | JIS H4000 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Tensile strength | 118.0 MPa | hot-rolled | JIS H4000 | |
Yield strength | 67.0 MPa | hot-rolled | JIS H4000 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.4e-05 1/K | Typical for Wrought 3000 Series Aluminium |
Melting point | 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium |
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium |
Thermal conductivity | 154.0 - 193.0 W/(m·K) | Typical for Wrought 3000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 4.2e-08 Ω·m | Typical for Wrought 3000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- JIS H4000 Grade 5154 Hot-Rolled Aluminium – Key Properties & Standards
- JIS H4000 Grade 3203O Aluminium – Properties & Standards
- JIS H4000 3203 H18 Aluminum Alloy – Premium 3000 Series Properties
- JIS H4000 Grade 5083 Hot‑Rolled Aluminium – Premium Mechanical Performance
- JIS H4000 Grade 1050 Hot-Rolled Aluminium: Superior Mechanical Properties
- JIS H4000 1070 Hot-Rolled Aluminium – Superior Strength & Durability
- High-Strength 1080 Grade JIS H4000 Hot-Rolled Aluminium – Ideal for Structural Applications
- JIS H4000 Grade 1200 Hot-Rolled Aluminium – Premium Properties & Performance
- JIS 3003 Hot-Rolled Aluminum – Durable, Corrosion-Resistant, and Easy to Machine
- JIS H4000 1100 Hot-Rolled Aluminum – High Corrosion Resistance & Purest Alloy