ASTM A276 Grade S20161: Annealed Austenitic Stainless Steel – Hot-Finished
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.9 - 8.2 g/cm³ | Typical for Austenitic Stainless Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 195 GPa | Typical for Austenitic Stainless Steel |
Elongation A50 | 23.0 °C | 40 % | |
Hardness, Brinell | 23.0 °C | 255 [-] | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Austenitic Stainless Steel |
Reduction of area | 23.0 °C | 40 % | |
Shear modulus | 23.0 °C | 77 GPa | Typical for Austenitic Stainless Steel |
Tensile strength | 23.0 °C | 860 MPa | |
Yield strength Rp0.2 | 23.0 °C | 345 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 1.9E-5 1/K | Typical for Austenitic Stainless Steel |
Melting point | 1230 - 1480 °C | Typical for Austenitic Stainless Steel | |
Specific heat capacity | 23.0 °C | 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
Thermal conductivity | 23.0 °C | 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.15 % |
Chromium | 15 - 18 % |
Manganese | 4 - 6 % |
Nickel | 4 - 6 % |
Nitrogen | 0.08 - 0.2 % |
Phosphorus | 0.05 % |
Silicon | 3 - 4 % |
Sulfur | 0.03 % |
Metal
- ASTM A479 Grade S20161 Annealed – Key Material Properties
- ASTM A276 Grade 446 Stainless Steel – Annealed, Cold‑Finished
- ASTM A276 Grade 446: High-Performance Annealed & Hot-Finished Stainless Steel
- ASTM A276 Grade XM-27: Annealed & Hot-Finished Ferritic Stainless Steel
- ASTM A276 Grade 444 Stainless Steel – Annealed, Cold-Finished
- ASTM A276 Grade 444 Stainless Steel – Annealed & Hot-Finished
- ASTM A276 Grade S40976 – High-Performance Annealed Stainless Steel (Hot‑Finished/Cold‑Finished)
- ASTM A276 Grade XM-27 Stainless Steel – Annealed & Cold-Finished
- ASTM A276 Grade S20161 – Annealed, Cold-Finished Austenitic Stainless Steel
- ASTM A276 S21800 Annealed Stainless Steel – Hot or Cold Finished