EN 10277‑4 Grade 20MnCrS5 – Ferritic‑Pearlitic Steel with Defined Hardness and Cold‑Drawn Finish

Steel 20MnCrS5 is compared to 20 MnCr 5 suitable for parts of higher dimension in vehicle and machine engineering at higher core strength and enhanced workability (gears, joint parts, gear wheels, bolts). Lowest application temperature -25°C, most favorable application area up to 80 mm nominal size. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Hardness, Brinell

20.0 °C

152 - 250 [-]

Poisson's ratio

20.0 °C

0.28 [-]

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.9 W/(m·K)

100.0 °C

46.4 W/(m·K)

200.0 °C

45.6 W/(m·K)

300.0 °C

43.5 W/(m·K)

400.0 °C

40.9 W/(m·K)

500.0 °C

38.2 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

12.7 mm²/s

100.0 °C

12 mm²/s

200.0 °C

11 mm²/s

300.0 °C

9.9 mm²/s

400.0 °C

8.7 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.27E-7 Ω·m

100.0 °C

2.76E-7 Ω·m

200.0 °C

3.46E-7 Ω·m

300.0 °C

4.31E-7 Ω·m

400.0 °C

5.32E-7 Ω·m

500.0 °C

6.48E-7 Ω·m

600.0 °C

7.81E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.17 - 0.22 %

Chromium

1 - 1.3 %

Manganese

1.1 - 1.4 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.02 - 0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-4 Grade 20MnCrS5 – Ferritic-Pearlitic Treated & Surface-Hardened Steel for High-Strength Automotive & Machinery Parts
    2. DIN 1652-3 Grade 20MoCrS4: Ferritic-Pearlite Structure & Cold-Drawn for High-Performance Applications
    3. DIN 1652-3 Grade 22CrMoS3-5: Ferritic‑Pearlite Heat Treatment & Cold‑Drawing for High‑Performance Automotive Components
    4. DIN 1652-3 Grade 20Cr4 Steel: Ferritic-Pearlitic Structure and Cold-Drawn Process for High-Wear Applications
    5. DIN 1652-3 Grade 20CrS4: Ferritic‑Pearlite Treatment & Cold‑Drawing for High‑Wear Applications
    6. DIN 1652-3 Grade 20MnCrS5: Ferritic-Pearlitic Structure and Cold-Drawn Processing
    7. DIN 1652‑3 Grade 20MoCr4 Steel – Ferritic‑Pearlite Structure & Cold‑Drawn for High‑Performance Applications
    8. DIN 1652-3 Grade 15CrNi6 – Ferritic‑Pearlite, Cold‑Drawn, High‑Toughness Steel for Vehicle Gears & Shafts
    9. EN 10277‑4 Grade 20NiCrMoS2‑2: Ferritic‑Pearlite Steel with Optimized Hardness and Cold‑Drawn Performance (+FP+C)
    10. EN 10277-4 Grade 16MnCrS5: Optimized Ferritic‑Pearlite Structure, Hardness Range, and Cold‑Drawn Performance