EN 12163 Grade CuZn28 R460 – Premium Copper Alloy for Automotive, Industrial & Electrical Applications
CuZn28 (CW504L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn20. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: good CuZn28 is used for deep drawing components and all types of sleeves, for automotive cooler, musical instruments, springing elements and clockfaces and as cladding material for ingot steel.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.55 - 8.6 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 114 GPa |
Shear modulus | 20.0 °C | 40 GPa |
Tensile strength | 20.0 °C | 460 MPa |
Yield strength Rp0.2 | 20.0 °C | 420 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 130 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.65E+7 S/m |
Electrical resistivity | 20.0 °C | 6.1E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.02 % |
Copper | 71 - 73 % |
Iron | 0.05 % |
Lead | 0.05 % |
Nickel | 0.3 % |
Tin | 0.1 % |
Metal
- EN 12163: CuZn28 H145 Wrought Copper Alloy – High Strength, Excellent Machinability
- EN 12163 CuZn28 H085 Wrought Copper Alloy – High Strength & Excellent Workability
- EN 12163 Grade CuZn28 H115: High-Performance Copper Alloy for Industrial Applications
- EN 12163 Grade CuZn33 R460 – High-Strength Unhardenable Copper Alloy for Precision Applications
- EN 12163 CuZn40Mn2Fe1 – R460 Grade: High-Strength, Corrosion-Resistant Copper Alloy
- EN 12163 Grade CuSn5 R460 – High-Performance Copper Tin Alloy for Precision Tubes
- EN 12163 Grade CuZn28 (R310) – Premium High‑Strength Copper Alloy
- EN 12163 Grade CuZn28 R370 – High-Performance Unhardenable Copper Alloy
- EN 12163 CuZn31Si1 R460 – Unhardenable Copper Alloy for Friction Components
- EN 12163 Grade CuZn30 (R460) – Premium Copper Alloy for Precision Applications