JIS H4040 Grade 5083 Aluminum Bar – 130 mm Diameter (5.118 in.) – Fabricated
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | |||
Elongation | 12.0 % | fabricated, diam. 130 mm, 5.118 in. | JIS H4040 | Bar | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 275.0 MPa | fabricated, diam. 130 mm, 5.118 in. | JIS H4040 | Bar | |
Yield strength | 108.0 MPa | fabricated, diam. 130 mm, 5.118 in. | JIS H4040 | Bar |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- JIS H4040 Grade 1070 Aluminium Alloy – Specs & Applications
- JIS H4040 Grade 1200 Aluminium – Premium Mechanical Properties
- JIS H4040 Grade 5056 Aluminium – Technical Overview
- JIS H4040 Grade 1050 Aluminium Alloy – Technical Specifications
- JIS H4100 5083 Aluminum Alloy – Key Mechanical Properties
- JIS H4000 5083-O Grade Aluminum Plate – Properties & Standards
- JIS H4040 Grade 5083 O – 5000 Series Aluminum Alloy Specification
- JIS H4040 Grade 6063: High-Performance Aluminum Alloy for Architecture
- JIS H4040 Grade 1100 – Pure Aluminum Alloy with Superior Corrosion Resistance
- JIS H4040 Grade 6063 T6 Aluminum Alloy – Corrosion-Resistant & Superior Finish