JIS G4305 Grade SUS429 Annealed – Properties & Performance

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.6 - 7.8 g/cm³	Typical for Ferritic Stainless Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	220 GPa	Typical for Ferritic Stainless Steel
Elongation A5	23.0 °C	22 %
Hardness, Brinell	23.0 °C	183 [-]
Hardness, Rockwell B	23.0 °C	88 [-]
Hardness, Vickers	23.0 °C	200 [-]
Poisson's ratio	23.0 °C	0.3 [-]	Typical for Ferritic Stainless Steel
Shear modulus	23.0 °C	77 GPa	Typical for Ferritic Stainless Steel
Tensile strength	23.0 °C	450 MPa
Yield strength Rp0.2	23.0 °C	205 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	9.3E-6 - 1.2E-5 1/K	Typical for Ferritic Stainless Steel
Melting point		1425 - 1530 °C	Typical for Ferritic Stainless Steel
Specific heat capacity	23.0 °C	420 - 586 J/(kg·K)	Typical for Ferritic Stainless Steel
Thermal conductivity	23.0 °C	11 - 22 W/(m·K)	Typical for Ferritic Stainless Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	6E-7 - 7.5E-7 Ω·m	Typical for Ferritic Stainless Steel

Technological properties

Property
Processing history	annealed