EN 12163 Grade CuAl11Fe6Ni6 R830 – High Strength Cold Formed Copper Alloy
CuAl11Fe6Ni6 (CW308G) is a wrought alloy of high strength, also at increased temperatures. The strength properties of cold formable wrought alloys are primarily dependent on the deformation grade. Tensile strength, yield strength and hardness rise according to the increasing cold forming grade. Elongation after fracture and contraction at fracture are decreasing. Thermal conductivity is reduced by the Al-content, electrical conductivity decreases according to the increasing AL-content. CuAl10Ni5Fe4 has a high strength at high temperatures up to approx. 300°C and a high endurance strength also at corrosion strain. The alloy has a particularly high strength as well as high corrosion and wear resistance to saltwater, sulfite bases and mineral acids. Processing properties: warm forming: good cold forming: unfavorable machinability: moderately soft soldering: unfavorable hard soldering: moderately gas-shielded welding: good burnishing: good The material is used for construction parts of higher strength, higher loaded bearing parts, pivot bearings at impact loading as well as for valves, valve seats, cover plates, link blocks, wear parts, die plates for chipless forming and for hot steam instruments.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.4 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 127 GPa | |
Elongation | 20.0 °C | 3 % | |
Elongation A11.3 | 20.0 °C | 2 % | |
Poisson's ratio | 23.0 °C | 0.33 [-] | Typical for Leaded Phosphor Bronze |
Shear modulus | 20.0 °C | 45 GPa | |
Tensile strength | 20.0 °C | 830 MPa | |
Yield strength Rp0.2 | 20.0 °C | 550 - 680 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 - 1.9E-5 1/K | Typical for Leaded Phosphor Bronze |
Specific heat capacity | 23.0 °C | 380 J/(kg·K) | Typical for Leaded Phosphor Bronze |
Thermal conductivity | 20.0 °C | 40 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 5.00E+6 S/m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 10.5 - 12.5 % |
Copper | 70.95 % |
Iron | 5 - 7 % |
Lead | 0.05 % |
Manganese | 1.5 % |
Nickel | 5 - 7 % |
Silicon | 0.2 % |
Tin | 0.1 % |
Zinc | 0.5 % |
Metal
- EN 12167 CuAl10Fe3Mn2 H130 – High‑Strength Cold‑Formed Alloy
- EN 12163 Grade CuAl10Fe3Mn2 H140 – Premium High-Strength Wrought Copper Alloy
- EN 12163 CuAl10Fe3Mn2 Alloy – High‑Strength, High‑Temperature Wrought Grade H170
- EN 12163 CuAl10Ni5Fe4 Wrought Alloy – High-Strength, Temperature-Resistant, Cold-Formable
- EN 12163 CuZn23Al6Mn4Fe3Pb (R780) – High-Strength, Seawater-Resistant Copper Alloy
- EN 12163 Grade CuAl10Fe3Mn2 R590 – High Strength, Temperature-Resistant Wrought Alloy
- EN 12163 Grade CuAl10Fe3Mn2 R690 – Premium High-Strength, Heat-Resistant Copper Alloy
- EN 12163 Grade CuAl10Ni5Fe4 R680: High-Strength Wrought Alloy
- EN 12163 CuAl10Ni5Fe4 R740 – High‑Strength, Thermally Conductive Cu‑Al Alloy
- EN 12163 CuAl10Ni5Fe4 (CW307G) Wrought Alloy – High Strength & Heat Resistance