DIN 17140-1 Grade D 83-2 Steel Wire Rod – Specifications & Properties
Non-alloy steel wire rod for cold drawing for general purpose rod
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.8 - 0.85 % |
Manganese | 0.3 - 0.7 % |
Phosphorus | 0.04 % |
Silicon | 0.1 - 0.3 % |
Sulfur | 0.04 % |
Metal
- DIN 17140-1 Grade D 20-2: High-Quality Non-Alloy Steel Wire Rod for Cold Drawing
- DIN 17140-1 Grade D 5-2: High-Quality Cold-Drawn Non‑Alloy Steel Wire Rod
- DIN 17140-1 Grade D 10-2 – High-Quality Low-Carbon Steel Wire Rod
- DIN 17140-1 Grade D 15‑2 – Premium Low‑Carbon Cold‑Drawn Steel Wire Rod
- DIN 17140‑1 Grade D 25‑2 – Premium Low‑Carbon Steel Wire Rod for Cold Drawing
- DIN 17140-1 Grade D 6-2: Premium Low‑Carbon Steel Wire Rod for Cold Drawing
- DIN 17140-1 Grade D 8-2 – Premium Non‑Alloy Steel Wire Rod for Cold Drawing
- DIN 17140-1 Grade D9 Wire Rod – Standard Low‑Carbon Steel for Cold Drawing
- DIN 488-1 Grade B500A – High-Ductility Reinforcing Steel
- DIN 488-1 Grade B500B Reinforcing Steel – Properties & Standards