Alloy 3 (C17510) – Premium TF00 Forging & Extrusion Solution
Alloy 3 from Materion Performance Alloys provides high electrical and thermal conductivity coupled with moderate strength.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.83 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 138 GPa |
Elongation | 23.0 °C | 10 - 25 % |
Hardness, Rockwell B | 23.0 °C | 92 - 100 [-] |
Tensile strength | 23.0 °C | 690 - 900 MPa |
Yield strength Rp0.2 | 23.0 °C | 550 - 690 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.76E-5 1/K |
Melting point | 1040 °C | |
Thermal conductivity | 23.0 °C | 240 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 2.9E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS |
Chemical properties
| Property | Value |
|---|---|
Beryllium | 0.2 - 0.6 % |
Copper | Balance |
Nickel | 1.4 - 2.2 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications for parts finished by forging or extrusion of these alloys include continuous casting mold components and resistance welding components. | |
Metal
- Alloy 10 (C17500) – TF00 Forging & Extrusion Performance Overview
- Alloy 3 (C17510) – High-Conductivity, Moderate-Strength Forging & Extrusion by Materion
- Alloy 25: High-Strength Copper Alloy for Forging & Extrusion – TB00 (C17200)
- Alloy 25 Forging & Extrusion – Highest Strength Copper Alloy (TF00 C17200)
- Alloy 165 Forging & Extrusion (TF00/C17000) – High Strength & Fatigue Resistance
- Alloy 3 (C17510) TF00 Wire – High Strength & Conductivity
- Alloy 3 (C17510) TF00 Tube – Premium Conductivity & Strength for Industrial Applications
- Alloy 3 (C17510) TF00 Plate – High Conductivity & Strength
- Alloy 3 (C17510) – Premium High-Conductivity Rod & Bar
- Alloy 3 (C17510) TF00 Strip – High Strength, Excellent Conductivity & Stress Relaxation Resistance