SAE J158 M4504 Air‑Quenched & Tempered Malleable Cast Iron – Enhanced Strength & Durability

Malleable iron is a cast iron in which the graphite is present as temper carbon nodules, instead of flakes as gray iron or spherulites as in ductile iron. M4505 is used where slightly higher strength and hardness than M3210 is needed.

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.2 - 7.34 g/cm³	Typical for Malleable Cast Iron

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	172 GPa
Elongation	23.0 °C	4 %
Hardness, Brinell	23.0 °C	163 - 217 [-]
Poisson's ratio	23.0 °C	0.27 [-]	Typical for Malleable Cast Iron
Shear modulus	23.0 °C	64 GPa	Typical for Malleable Cast Iron
Tensile strength	23.0 °C	448 MPa
Yield strength	23.0 °C	310 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1E-5 - 1.4E-5 1/K	Typical for Malleable Cast Iron
Melting point		1120 °C	Typical for Cast Iron
Specific heat capacity	23.0 °C	460 - 527 J/(kg·K)	Typical for Malleable Cast Iron
Thermal conductivity	23.0 °C	51 W/(m·K)	Typical for Malleable Cast Iron

Chemical properties

Property	Value	Comment
Carbon	2.2 - 2.9 %
Iron	93.6 - 96.71 %	balance
Manganese	0.15 - 1.25 %
Phosphorus	0.02 - 0.1 %
Silicon	0.9 - 1.9 %
Sulfur	0.02 - 0.2 %

Technological properties

Property
Application areas	Certain compressor crankshafts and hubs
Processing history	as agreed

AA Standards Grade 2008 T4: Detailed Mechanical and Physical Properties SAE J158 Grade M5003: Air‑Quenched & Tempered Malleable Cast Iron