JIS 5052 T32 Aluminum Alloy – Superior Corrosion Resistance & Welding Performance

Aluminum JIS 5052 is a non-heat treatable alloy with excellent finishing qualities. JIS 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.

Properties

General

Property	Value	Comment
Density	2.65 - 2.7 g/cm³	Typical for Wrought 5000 Series Aluminium

Mechanical

Property	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	69.0 - 70.0 GPa				Typical for Wrought 5000 Series Aluminium
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]				Typical for Wrought 5000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa				Typical for Wrought 5000 Series Aluminium
Tensile strength	216.0 MPa	T32	JIS H4120	Wire

Thermal

Property	Value	Comment
Coefficient of thermal expansion	2.2e-05 - 2.5e-05 1/K	Typical for Wrought 5000 Series Aluminium
Max service temperature	150.0 °C	Typical for Wrought 5000 Series Aluminium
Melting point	560.0 - 655.0 °C	Typical for Wrought 5000 Series Aluminium
Specific heat capacity	879.0 - 963.0 J/(kg·K)	Typical for Wrought 5000 Series Aluminium
Thermal conductivity	112.0 - 205.0 W/(m·K)	Typical for Wrought 5000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	18000000.0 - 31000000.0 S/m	Typical for Wrought 5000 Series Aluminium
Electrical resistivity	3.3e-08 - 5e-08 Ω·m	Typical for Wrought 5000 Series Aluminium

Technological properties

Property
Processing history	T32
Workability	Good workability.

Property

Processing history

T32

Workability

Good workability.