EN 12164 Grade CuZn40Mn1Pb1AlFeSn (R500) – Premium Brass for Industrial Applications
Material CuZn40Mn1Pb1AlFeSn (CW721R) is used in the form of rods, hollow rods, profiles, forging prematerial and forged parts.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.3 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 96 GPa | |
Elongation | 20.0 °C | 12 - 14 % | |
Elongation A100 | 20.0 °C | 5 % | |
Elongation A11.3 | 20.0 °C | 10 % | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 500 - 590 MPa | |
Yield strength Rp0.2 | 20.0 °C | 250 - 370 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 - 2.1E-5 1/K | Typical for Wrought Copper Brass |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 88 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 9.00E+6 S/m |
Specific Electrical conductivity | 15.5 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.3 - 1.3 % |
Copper | 57 - 59 % |
Iron | 0.2 - 1.2 % |
Lead | 0.8 - 1.6 % |
Manganese | 0.8 - 1.8 % |
Nickel | 0.3 % |
Tin | 0.2 - 1 % |
Metal
- EN 12164 Grade CuZn40Mn1Pb1 R500 – High-Performance Unhardenable Copper Alloy for Bearings
- EN 12164 CuZn38Pb1 (R490) Brass – Key Mechanical & Thermal Properties
- EN 12164 Grade CuZn38Pb2 R490 – Premium Wrought Copper Brass Specification
- EN 12164 CuZn40Mn1Pb1AlFeSn R450 Brass – High Strength, Low Lead, Ideal for Forged Parts
- EN 12164 Lead Phosphor Bronze CuZn21Si3P – R500 Grade: High Strength & Corrosion Resistance
- EN 12164 CuZn40Mn1Pb1AlFeSn Brass Grade R440 – Specifications & Performance
- EN 12164 CuZn40Mn1Pb1AlFeSn Brass – R460 Grade, High Strength & Corrosion Resistance
- EN 12164 Grade CuZn40Mn1Pb1AlFeSn – High-Strength Wrought Copper Brass (R520)
- EN 12164 CuZn39Pb3 R500 Brass: Properties, Strength & Corrosion Resistance
- EN 12164 Grade CuZn40Pb2 R500 – Lead-Enhanced Copper Alloy for Superior Machinability