ASTM A513 Grade 1008 Normalized Low-Carbon Steel: Key Properties & Specs

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.8 - 7.9 g/cm³	Typical for Low Carbon Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	200 - 215 GPa	Typical for Low Carbon Steel
Elongation A50	23.0 °C	30 %
Hardness, Rockwell B	23.0 °C	65 [-]
Poisson's ratio	23.0 °C	0.29 [-]	Typical for Low Carbon Steel
Shear modulus	23.0 °C	82 GPa	Typical for Low Carbon Steel
Tensile strength	23.0 °C	260 MPa
Yield strength	23.0 °C	160 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Max service temperature		500 °C	Typical for Carbon Steel
Melting point		1480 - 1526 °C	Typical for Low Carbon Steel
Specific heat capacity	23.0 °C	465 J/(kg·K)	Typical for Low Carbon Steel
Thermal conductivity	23.0 °C	25 - 93 W/(m·K)	Typical for Low Carbon Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Magnetic

Property	Value	Comment
Curie temperature	770 °C	Typical for Low Carbon Steel

Chemical properties

Property	Value
Carbon	0.1 %
Manganese	0.5 %
Phosphorus	0.04 %
Sulfur	0.035 %

ASTM A513 Grade 1008 Stress-Relieved DOM Low Carbon Steel – Superior Mechanical Properties ASTM A513 Grade 1010 As-Welded Steel – Key Properties & Applications