ASTM A350 LF2 Class 1 Heat-Treated Steel – Premium Low Carbon Grade
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy | 23.0 °C | 20 J | |
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A50 | 23.0 °C | 30 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Reduction of area | 23.0 °C | 30 % | |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 23.0 °C | 485 - 655 MPa | |
Yield strength Rp0.2 | 23.0 °C | 250 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.3 % |
Chromium | 0.3 % |
Copper | 0.4 % |
Manganese | 0.6 - 1.35 % |
Molybdenum | 0.12 % |
Nickel | 0.4 % |
Niobium | 0.02 % |
Phosphorus | 0.04 % |
Silicon | 0.15 - 0.3 % |
Sulfur | 0.04 % |
Vanadium | 0.08 % |
Metal
- ASTM A214 Grade A214 Heat‑Treated Steel: Key Properties & Specifications
- ASTM A240 Grade S40920 Heat‑Treated Stainless Steel – Premium Ferritic Properties
- ASTM A240 Grade S40930 Heat‑Treated Stainless Steel – Premium Performance
- ASTM A240 S40975 Heat‑Treated Ferritic Stainless Steel – Key Properties
- ASTM A240 Grade S41003 – Heat‑Treated Ferritic Stainless Steel – Key Mechanical & Physical Properties
- Heat-Treated ASTM A487 Grade CA6NM Class B Stainless Steel – Superior Performance
- ASTM A350 Grade LF1 Class 1 Heat‑Treated Steel – Premium Medium‑Carbon Performance
- ASTM A958 SC1020 65/35 Heat‑Treated Low‑Carbon Steel – Key Properties & Specifications
- ASTM A958 SC1025 65/35 Heat‑Treated Low Carbon Steel – High Strength
- ASTM A335 Grade P1 Heat‑Treated Steel – Properties & Performance