ASTM A311 Grade 1117 – Cold Drawn, Stress‑Relief Annealed Steel for High‑Performance Applications
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Elongation A50 | 23.0 °C | 12 - 15 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Reduction of area | 23.0 °C | 30 - 40 % | |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 23.0 °C | 415 - 520 MPa | |
Yield strength | 23.0 °C | 345 - 450 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.14 - 0.2 % |
Manganese | 1 - 1.3 % |
Phosphorus | 0.04 % |
Sulfur | 0.08 - 0.13 % |
Metal
- ASTM A311 Grade 1541: Cold‑Drawn & Stress‑Relieved Steel – Quality, Reliability, and Performance
- ASTM A311 Grade 1045: Cold Drawn & Stress-Relief Annealed Steel – Performance Specs
- ASTM A311 Grade 1050: Cold‑Drawn & Stress‑Relief Annealed Steel
- ASTM A311 Grade 1141 – Cold‑Drawn & Stress‑Relief Annealed Steel for Superior Performance
- ASTM A311 Grade 1035: Cold Drawn, Stress‑Relief Annealed Steel – Normal Draft
- EN 10277-5 Grade 42CrMoS4 Soft Annealed & Cold Drawn (A+C) – High-Performance Steel for Automotive & Machine Applications
- EN 10277-4: Grade 20MnCrS5 Soft‑Annealed and Cold‑Drawn Steel (+A+C)
- 25CrMo4 Steel – EN 10277-5 Cold Drawn, Soft Annealed, High Strength & Ductility
- EN 10277-5 Grade 25CrMoS4 – Cold‑Drawn, Turned & Soft‑Annealed High‑Strength Steel
- ASTM A311 1018 Steel – Cold‑Drawn, Stress‑Relieved & Annealed for Superior Performance