ASTM B241 Grade 6061 T4 Aluminum Alloy – High Performance & Corrosion Resistance

ASTM 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.

Quantity: 1 PCS

Properties

General

Property	Value	Comment
Density	2.7 g/cm³	Typical for Wrought 6000 Series Aluminium

Mechanical

Property	Value	Comment
Elastic modulus	70.0 GPa	Typical for Wrought 6000 Series Aluminium
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m	Typical for Wrought 6000 Series Aluminium
Poisson's ratio	0.33 [-]	Typical for Wrought 6000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa	Typical for Wrought 6000 Series Aluminium

Thermal

Property	Value	Comment
Coefficient of thermal expansion	1.6e-05 - 2.4e-05 1/K	Typical for Wrought 6000 Series Aluminium
Melting point	555.0 - 655.0 °C	Typical for Wrought 6000 Series Aluminium
Specific heat capacity	887.0 - 963.0 J/(kg·K)	Typical for Wrought 6000 Series Aluminium
Thermal conductivity	170.0 - 220.0 W/(m·K)	Typical for Wrought 6000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
Electrical resistivity	2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.04 - 0.35 %	T4	ASTM B241	Tube
Copper	0.15 - 0.4 %	T4	ASTM B241	Tube
Iron	0.7	T4	ASTM B241	Tube
Magnesium	0.8 - 1.2 %	T4	ASTM B241	Tube
Manganese	0.15	T4	ASTM B241	Tube
Silicon	0.4 - 0.8 %	T4	ASTM B241	Tube
Titanium	0.15	T4	ASTM B241	Tube
Zinc	0.25	T4	ASTM B241	Tube

Technological properties

Property
Workability	Excellent workability.

Property

Workability

Excellent workability.