EN 573-3 Grade 3.3206 T39 – Premium Aluminium Alloy for High-Performance Applications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | T39 | EN 573-3, EN 1301 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.5 GPa | T39 | EN 573-3, EN 1301 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.1 GPa | T39 | EN 573-3, EN 1301 | |
Tensile strength | 220.0 MPa | T39 | EN 573-3, EN 1301 | |
270.0 MPa | T39 | EN 573-3, EN 1301 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.18e-05 1/K | T39 | EN 573-3, EN 1301 |
20 °C | 2.18e-05 1/K | T39 | EN 573-3, EN 1301 | |
20 °C | 2.3399999999999996e-05 1/K | T39 | EN 573-3, EN 1301 | |
20 °C | 2.45e-05 1/K | T39 | EN 573-3, EN 1301 | |
20 °C | 2.56e-05 1/K | T39 | EN 573-3, EN 1301 | |
100 °C | 2.3399999999999996e-05 1/K | T39 | EN 573-3, EN 1301 | |
200 °C | 2.45e-05 1/K | T39 | EN 573-3, EN 1301 | |
300 °C | 2.56e-05 1/K | T39 | EN 573-3, EN 1301 | |
Melting point | 585.0 - 650.0 °C | T39 | EN 573-3, EN 1301 | |
Specific heat capacity | 898.0 J/(kg·K) | T39 | EN 573-3, EN 1301 | |
Thermal conductivity | 200.0 - 220.0 W/(m·K) | T39 | EN 573-3, EN 1301 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 34000000.0 - 38000000.0 S/m | T39 | EN 573-3, EN 1301 |
Electrical resistivity | 2.63e-08 - 2.94e-08 Ω·m | T39 | EN 573-3, EN 1301 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.05 % | T39 | EN 573-3, EN 1301 |
Copper | 0.1 % | T39 | EN 573-3, EN 1301 |
Iron | 0.1 - 0.3 % | T39 | EN 573-3, EN 1301 |
Magnesium | 0.35 - 0.6 % | T39 | EN 573-3, EN 1301 |
Manganese | 0.1 % | T39 | EN 573-3, EN 1301 |
Silicon | 0.3 - 0.6 % | T39 | EN 573-3, EN 1301 |
Titanium | 0.1 % | T39 | EN 573-3, EN 1301 |
Zinc | 0.15 % | T39 | EN 573-3, EN 1301 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: EQ: sehr gut, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / good, friction soldering: very good, soft brazing with flux: good | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / -, Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) - / good (O) | |
Metal
- EN 573-3 Grade 3.3206 T89 Aluminium Properties – Strength, Toughness & More
- EN 573-3 Grade 3.2315 T39 Aluminium Alloy – Key Mechanical Properties
- EN 573-3 Grade 3.3206 F: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.3206 H18 – Detailed Material Properties & Standards
- EN 573-3 Grade 3.3206 H19 – High-Performance Aluminium Alloy
- EN 573-3 Grade 3.3206 O – Aluminium Alloy Specifications & Properties
- EN 573-3 Grade 3.3206 T64 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.3206 T66 – Aluminium Alloy Technical Overview
- EN 573-3 Grade 3.3211 T39 – Premium Anodizable Aluminum Alloy
- EN 573-3 AW-6063 T39 Aluminum Alloy – High Corrosion Resistance & Superior Finish