AA 6053 H13 Aluminum Alloy: Technical Specs & Standards
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.69 g/cm³ | H13 | AA Standards, ASTM B316 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 130.0 - 180.0 MPa | H13 | AA Standards, ASTM B316 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | H13 | AA Standards, ASTM B316 | |
100 °C | 2.3e-05 1/K | H13 | AA Standards, ASTM B316 | ||
Melting point | 575.0 - 650.0 °C | H13 | AA Standards, ASTM B316 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 155.0 - 172.0 W/(m·K) | H13 | AA Standards, ASTM B316 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 23000000.0 - 26000000.0 S/m | H13 | AA Standards, ASTM B316 |
Electrical resistivity | 3.85e-08 - 4.35e-08 Ω·m | H13 | AA Standards, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 - 0.35 % | H13 | AA Standards, ASTM B316 |
Copper | 0.1 % | H13 | AA Standards, ASTM B316 |
Iron | 0.35 % | H13 | AA Standards, ASTM B316 |
Magnesium | 1.1 - 1.4 % | H13 | AA Standards, ASTM B316 |
Zinc | 0.1 % | H13 | AA Standards, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (T6, T61), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O), sufficient (T6, T61) | |
| Workability | Excellent workability. | |
Metal
- AA Standards Grade 6053 O – Detailed Material Properties
- AA Standards Grade 2117 H13 – Aluminium Alloy Specification
- AA Standard Grade 6053 T61: Technical Specifications & Material Properties
- AA 2017 H13 Aluminum Alloy: Strength, Ductility, and Machinability Explained
- AA 2024 H13 Aluminum Alloy – Industrial Strength & Machinability
- AA 2219 H13 Aluminum Alloy: Premium Grade for High-Performance Applications
- AA 6061 H13 Aluminum Alloy – High Strength, Corrosion Resistant, and Easily Welded
- AA 7050 H13: High-Strength, Heat-Treatable Aluminium for Aerospace Applications
- High-Strength AA 7075 H13 Aluminum Alloy – Aerospace Grade
- AA 7178 H13 Aluminium Alloy – High Strength & Versatility