JIS H4040 Grade 6061 T4 Aluminum: Superior Corrosion Resistance & Weldability

JIS 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.

Quantity: 1 PCS

Properties

General

Property	Value	Comment
Density	2.7 g/cm³	Typical for Wrought 6000 Series Aluminium

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	70.0 GPa			Typical for Wrought 6000 Series Aluminium
Elongation	16.0 %	T4	JIS H4040
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 6000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 6000 Series Aluminium
Shear modulus	26.0 - 26.5 GPa			Typical for Wrought 6000 Series Aluminium
Tensile strength	177.0 MPa	T4	JIS H4040
Yield strength	108.0 MPa	T4	JIS H4040

Thermal

Property	Value	Comment
Coefficient of thermal expansion	1.6e-05 - 2.4e-05 1/K	Typical for Wrought 6000 Series Aluminium
Melting point	555.0 - 655.0 °C	Typical for Wrought 6000 Series Aluminium
Specific heat capacity	887.0 - 963.0 J/(kg·K)	Typical for Wrought 6000 Series Aluminium
Thermal conductivity	170.0 - 220.0 W/(m·K)	Typical for Wrought 6000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
Electrical resistivity	2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Technological properties

Property
Processing history	T4
Workability	Excellent workability.

Property

Processing history

Workability

Excellent workability.