JIS H4080 Grade 2014 T4 Aluminum Alloy – Superior Strength & Machinability

JIS 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy JIS 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Properties

General

Property	Value	Comment
Density	2.75 - 2.84 g/cm³	Typical for Wrought 2000 Series Aluminium

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	70.0 - 73.0 GPa			Typical for Wrought 2000 Series Aluminium
Elongation	12.0 %	T4	JIS H4080
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 2000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 2000 Series Aluminium
Shear modulus	26.0 - 27.5 GPa			Typical for Wrought 2000 Series Aluminium
Tensile strength	343.0 MPa	T4	JIS H4080
Yield strength	245.0 MPa	T4	JIS H4080

Thermal

Property	Value	Comment
Coefficient of thermal expansion	1.6e-05 - 2.4e-05 1/K	Typical for Wrought 2000 Series Aluminium
Melting point	500.0 - 650.0 °C	Typical for Wrought 2000 Series Aluminium
Specific heat capacity	816.0 - 963.0 J/(kg·K)	Typical for Wrought 2000 Series Aluminium
Thermal conductivity	112.0 - 251.0 W/(m·K)	Typical for Wrought 2000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	18000000.0 - 30000000.0 S/m	Typical for Wrought 2000 Series Aluminium
Electrical resistivity	3.4e-08 - 6e-08 Ω·m	Typical for Wrought 2000 Series Aluminium

Technological properties

Property
Processing history	T4
Workability	Moderate Workability

Property

Processing history

Workability

Moderate Workability

JIS H4080 2014 O Grade Aluminum Alloy – High Strength & Weldability JIS H4080 2014 T6 Aluminum – High Strength & Machinability