EN 1706 Grade AC-43000 T5 Aluminium Casting Alloy – Properties & Standards
Aluminium casting alloy (sand casting, permanent mould casting)
Properties
General
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Density | 20.0 °C | 2.65 g/cm³ | T5 | EN 1706 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 74.0 GPa | T5 | EN 1706 | |
Elongation | -196.0 °C | 0.6 % | T5 | EN 1706 | |
-196.0 °C | 2.4 % | T5 | EN 1706 | ||
-120.0 °C | 0.5 % | T5 | EN 1706 | ||
-120.0 °C | 2.4 % | T5 | EN 1706 | ||
-50.0 °C | 1.0 % | T5 | EN 1706 | ||
-50.0 °C | 2.4 % | T5 | EN 1706 | ||
20.0 °C | 0.8 % | T5 | EN 1706 | ||
20.0 °C | 2.2 % | T5 | EN 1706 | ||
20.0 °C | 2.2 - 2.4 % | T5 | EN 1706 | ||
20.0 °C | 2.4 % | T5 | EN 1706 | ||
220.0 °C | 10.6 % | T5 | EN 1706 | ||
220.0 °C | 28.4 % | T5 | EN 1706 | ||
280.0 °C | 30.1 % | T5 | EN 1706 | ||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Tensile strength | -196.0 °C | 277.0 MPa | T5 | EN 1706 | |
-196.0 °C | 304.0 MPa | T5 | EN 1706 | ||
-120.0 °C | 256.0 MPa | T5 | EN 1706 | ||
-120.0 °C | 275.0 MPa | T5 | EN 1706 | ||
-50.0 °C | 246.0 MPa | T5 | EN 1706 | ||
-50.0 °C | 263.0 MPa | T5 | EN 1706 | ||
20.0 °C | 235.0 - 251.0 MPa | T5 | EN 1706 | ||
20.0 °C | 235.0 MPa | T5 | EN 1706 | ||
20.0 °C | 241.0 MPa | T5 | EN 1706 | ||
20.0 °C | 241.0 - 304.0 MPa | T5 | EN 1706 | ||
20.0 °C | 251.0 MPa | T5 | EN 1706 | ||
20.0 °C | 304.0 MPa | T5 | EN 1706 | ||
220.0 °C | 68.0 MPa | T5 | EN 1706 | ||
220.0 °C | 75.0 MPa | T5 | EN 1706 | ||
280.0 °C | 48.0 MPa | T5 | EN 1706 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.1e-05 1/K | T5 | EN 1706 | |
Melting point | 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | |||
Specific heat capacity | 20.0 °C | 910.0 J/(kg·K) | T5 | EN 1706 | |
Thermal conductivity | 20.0 °C | 150.0 - 170.0 W/(m·K) | T5 | EN 1706 |
Electrical
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 19000000.0 - 25000000.0 S/m | T5 | EN 1706 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 86.95 % | T5 | EN 1706 |
Copper | 0.05 | T5 | EN 1706 |
Iron | 0.55 | T5 | EN 1706 |
Lead | 0.05 | T5 | EN 1706 |
Magnesium | 0.2 - 0.45 % | T5 | EN 1706 |
Manganese | 0.45 | T5 | EN 1706 |
Nickel | 0.05 | T5 | EN 1706 |
Silicon | 9.0 - 11.0 % | T5 | EN 1706 |
Tin | 0.05 | T5 | EN 1706 |
Titanium | 0.15 | T5 | EN 1706 |
Zinc | 0.1 | T5 | EN 1706 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | permanent mould casting | |
Metal
- EN 1706 Grade 3.1841 T6 Aluminium: Key Properties & Standards
- EN 1706 Grade 3.1841 T64 Aluminium Alloy – Key Properties & Standards
- AC-43300 T64 Aluminium Alloy – EN 1706 Grade with Enhanced Mechanical Properties
- EN 1706 Grade 3.2373 T6 – Aluminium Alloy Specifications
- EN 1706 Grade 3.2381 T6 – Key Mechanical Properties & Standards
- EN 1706 Grade 3.2385 F – Full Technical Data & Mechanical Properties
- EN 1706 Grade 3.2385 T6 Aluminium Alloy – Key Properties & Standards
- EN 1706 Grade AC-43000 F Aluminium Alloy – Key Properties & Standards
- EN 1706 Grade AC-43000 T6 Aluminium Casting Alloy – Specs & Performance
- EN 1706 Certified AC-43000 T64 Aluminium Alloy – Ideal for Sand & Permanent Mould Casting