ASTM B316 Grade 3003 H14: High-Quality Aluminum Alloy for Corrosion Resistance & Strength
Aluminum ASTM 3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, ASTM 3003 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.72 - 2.73 g/cm³ | Typical for Wrought 3000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.5 - 70.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Tensile strength | 135.0 - 180.0 MPa | H14 | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.4e-05 1/K | Typical for Wrought 3000 Series Aluminium |
Melting point | 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium |
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium |
Thermal conductivity | 154.0 - 193.0 W/(m·K) | Typical for Wrought 3000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 4.2e-08 Ω·m | Typical for Wrought 3000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Copper | 0.05 - 0.2 % | H14 | ASTM B316 | Wire, Rod |
Iron | 0.7 | H14 | ASTM B316 | Wire, Rod |
Manganese | 1.0 - 1.5 % | H14 | ASTM B316 | Wire, Rod |
Silicon | 0.6 | H14 | ASTM B316 | Wire, Rod |
Zinc | 0.1 | H14 | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B211 Grade 3003 H14 Aluminum: Corrosion‑Resistant, Weldable, High‑Strength Alloy
- ASTM B316 Grade 3003O Aluminum Alloy: High Corrosion Resistance & Easy Welding
- ASTM B316 Grade 2017 Aluminum Alloy – Strength, Ductility & Machinability
- ASTM B316 Grade 5005 O – High-Performance Aluminum Alloy for Marine and Industrial Use
- ASTM B316 Grade 1100 H14 – Premium Corrosion-Resistant Aluminum Alloy
- ASTM B316 Grade 5052‑O Aluminum Alloy: Superior Corrosion Resistance & Welding Performance
- ASTM B483 Grade 3003 H14 Aluminum Alloy: Corrosion‑Resistant, Machinable & Weldable
- ASTM B210 Grade 3003 H14 Aluminum: Corrosion-Resistant, Weldable, and Machinable Alloy
- AA 3003 H14 Aluminum Alloy – High Corrosion Resistance & Superior Machinability