DIN 17222 Ck60: Premium Cold‑Rolled & Hardened Steel for Precision Springs
The steel Ck 60 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 2.0 mm thicknesses.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.8 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 206 - 212 GPa | ||
100.0 °C | 207 GPa | ||
200.0 °C | 199 GPa | ||
300.0 °C | 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Hardness, Vickers | 20.0 °C | 670 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for High Carbon Steel |
Shear modulus | 20.0 °C | 78 GPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.08E-5 1/K | |
20.0 °C | 1.19E-5 1/K | ||
100.0 °C | 1.25E-5 1/K | ||
200.0 °C | 1.3E-5 1/K | ||
300.0 °C | 1.36E-5 1/K | ||
400.0 °C | 1.41E-5 1/K | ||
500.0 °C | 1.45E-5 1/K | ||
600.0 °C | 1.49E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1289 - 1478 °C | Typical for High Carbon Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 41.7 W/(m·K) | |
100.0 °C | 43.4 W/(m·K) | ||
200.0 °C | 43.2 W/(m·K) | ||
300.0 °C | 41.4 W/(m·K) | ||
400.0 °C | 39.1 W/(m·K) | ||
500.0 °C | 36.7 W/(m·K) | ||
600.0 °C | 34.1 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11.6 mm²/s | |
100.0 °C | 11.3 mm²/s | ||
200.0 °C | 10.5 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.3 mm²/s | ||
500.0 °C | 7.1 mm²/s | ||
600.0 °C | 5.8 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 2.5E-7 Ω·m |
100.0 °C | 2.95E-7 Ω·m | |
200.0 °C | 3.65E-7 Ω·m | |
300.0 °C | 4.53E-7 Ω·m | |
400.0 °C | 5.56E-7 Ω·m | |
500.0 °C | 6.74E-7 Ω·m | |
600.0 °C | 8.13E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.57 - 0.65 % |
Manganese | 0.6 - 0.9 % |
Phosphorus | 0.04 % |
Silicon | 0.15 - 0.35 % |
Sulfur | 0.035 % |
Technological properties
| Property | ||
|---|---|---|
| Features | Spring | |
Metal
- DIN 17222: Grade 55Si7 Cold‑Rolled & Hardened Steel – Precision Spring Material
- DIN 17222 Grade 71Si7: Premium Cold‑Rolled & Hardened Steel for High‑Load Tension Springs
- DIN 17222 Grade 50CrV4: Precision Cold‑Rolled & Hardened Steel for Springs
- DIN 17222 Grade 67SiCr5 Cold-Rolled & Hardened Steel for Precision Springs
- DIN 17222 Grade C55 Cold-Rolled & Hardened Steel – Precision Springs
- DIN 17222 C60 Cold-Rolled & Hardened Steel – Premium Spring Strip Grade
- DIN 17222 Grade C67: Cold-Rolled & Hardened Steel for Precision Springs
- DIN 17222 C75 Cold‑Rolled & Hardened Steel – Precision Springs
- DIN 17222 Grade Ck55: Cold‑Rolled & Hardened Steel for High‑Precision Springs
- DIN 17222 Grade Ck67 Cold‑Rolled & Hardened Steel – Superior Spring Material