EN 12164 R430 Brass (CuZn39Pb3) – High Strength, Excellent Machinability
Material CuZn39Pb3, mat. No. CW614N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb3, mat. No. 2.0401 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for unleaded brass of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: Main alloy of the brass materials for machining on automats. Use for all types of form turning parts, in precision engineering as well as in watch and electrical industry.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 - 8.47 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 96 - 97 GPa | |
Elongation | 20.0 °C | 10 - 12 % | |
Elongation A10 | 20.0 °C | 8 % | |
Elongation A100 | 20.0 °C | 6 - 8 % | |
Elongation A11.3 | 20.0 °C | 8 - 10 % | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 430 MPa | |
Yield strength Rp0.2 | 20.0 °C | 6 - 250 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.93E-5 1/K | |
200.0 °C | 2.1E-5 1/K | ||
300.0 °C | 2.14E-5 1/K | ||
800.0 °C | 2.47E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | -200.0 °C | 50 W/(m·K) | |
20.0 °C | 113 - 123 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.46E+7 - 1.50E+7 S/m |
200.0 °C | 1.20E+7 S/m | |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m |
200.0 °C | 8.3E-8 Ω·m | |
Specific Electrical conductivity | 25 - 25.2 % IACS | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 57 - 59 % |
Iron | 0.3 % |
Lead | 2.5 - 3.5 % |
Nickel | 0.3 % |
Tin | 0.3 % |
Metal
- EN 12163 Copper Alloy CuZn32Pb2AsFeSi (R430) – High Strength Rods
- EN 12164 CuZn38Pb1 (R490) Brass – Key Mechanical & Thermal Properties
- EN 12164 Grade CuZn38Pb2 R490 – Premium Wrought Copper Brass Specification
- EN 12164 Grade CuZn39Pb2 M – Lead-Enhanced Brass Alloy for Durable Applications
- EN 12164 Grade CuZn39Pb3 R550 – High-Strength, Lead-Enhanced Brass Alloy
- EN 12164 R380 CuZn39Pb3 Brass – High Strength, Low Lead Alloy
- EN 12164 Grade CuZn39Pb3 R400 – High-Performance Brass Alloy
- EN 12164 R360 CuZn39Pb3 Brass – Unhardenable Alloy with High Strength and Improved Machinability
- EN 12164 CuZn39Pb3 R500 Brass: Properties, Strength & Corrosion Resistance
- EN 12164 R430 – CuZn40Pb2 Leaded Brass: Superior Machinability & Cold‑Forming Performance