EN 12166 CuZn39Pb2 (H01) – Lead-Enhanced Brass for High Strength & Machinability
Material CuZn39Pb2, mat. No. CW612N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb2, mat. No. 2.0380 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: unfavorable machinability: very good hard soldering: moderately soft soldering: very good TIG-welding: unfavorable burnishing: very good Application: For components in precision mechanics, machine and apparatus engineering as well as for circuit boards and clockwerks for watch industry.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 - 8.45 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 102 GPa | |
Elongation | 20.0 °C | 20 % | |
Elongation A10 | 20.0 °C | 15 % | |
Elongation A100 | 20.0 °C | 10 % | |
Hardness, Vickers | 20.0 °C | 100 - 140 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Tensile strength | 20.0 °C | 380 - 400 MPa | |
Yield strength Rp0.2 | 20.0 °C | 180 - 200 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2E-5 1/K | |
300.0 °C | 2.1E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 109 - 117 W/(m·K) | |
200.0 °C | 134 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.39E+7 - 1.40E+7 S/m |
200.0 °C | 1.10E+7 S/m | |
Electrical resistivity | 20.0 °C | 7.1E-8 Ω·m |
200.0 °C | 9.1E-8 Ω·m | |
Specific Electrical conductivity | 24 % IACS | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 59 - 60 % |
Iron | 0.3 % |
Lead | 1.6 - 2.5 % |
Nickel | 0.3 % |
Tin | 0.3 % |
Metal
- EN 12166 Grade CuNi18Zn20 H01 – High Strength, Corrosion-Resistant Copper–Nickel–Zinc Alloy
- EN 12166 Grade CuNi10Zn27 H01: High-Performance Copper-Nickel-Zinc Alloy Wire
- EN 12166 CuNi12Zn24 H01 – High Strength, Corrosion-Resistant Copper-Nickel-Zinc Alloy
- EN 12166 Grade CuZn38Pb2 H01 – Wrought Copper‑Brass Alloy Specification
- EN 12166 CuZn39Pb2 H130 – Premium Copper Alloy Wire for General Use
- EN 12166 Grade CuZn39Pb2 H100 – Leaded Brass Alloy Specifications
- EN 12166 CuZn39Pb2 H070 – Premium Leaded Brass Alloy for Cold Forming
- EN 12166: CuZn37 H01 – Premium Copper Alloy for Cold Forming Applications
- EN 12166 Grade CuZn36 H01 – Premium Copper Alloy for Precision Engineering
- EN 12166 Grade CuSn5 H01 – Premium CuSn5 Alloy for Springs & Connectors