DIN 1652-3 Grade Cm15: Normalized or Normalized Formed Steel – Key Properties & Applications

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

24 %

100.0 °C

24 %

150.0 °C

24 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

55 %

100.0 °C

55 %

150.0 °C

55 %

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

400 - 530 MPa

Yield strength

20.0 °C

230 MPa

Yield strength Rp0.2

100.0 °C

210 MPa

150.0 °C

200 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

57.5 W/(m·K)

100.0 °C

55.7 W/(m·K)

200.0 °C

51.9 W/(m·K)

300.0 °C

47.6 W/(m·K)

400.0 °C

43.4 W/(m·K)

500.0 °C

39.6 W/(m·K)

600.0 °C

36 W/(m·K)

Thermal diffusivity

20.0 °C

15.9 mm²/s

100.0 °C

14.3 mm²/s

200.0 °C

12.5 mm²/s

300.0 °C

10.8 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.6 mm²/s

600.0 °C

6.1 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.1E-7 Ω·m

100.0 °C

2.3E-7 Ω·m

200.0 °C

3.04E-7 Ω·m

300.0 °C

3.94E-7 Ω·m

400.0 °C

5.01E-7 Ω·m

500.0 °C

6.25E-7 Ω·m

600.0 °C

7.7E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Aluminium

0.02 - 0.05 %

Carbon

0.12 - 0.18 %

Manganese

0.3 - 0.6 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.02 - 0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
    2. DIN 17240 Grade C35 Steel – Normalized or Normalized‑Formed (+N) for Creep Resistance up to 400 °C
    3. DIN 2395‑3 Grade M22 Tubes – Normalized & Normalized‑Formed (N)
    4. DIN 2391-2: Grade St 30 Al Seamless Steel Tubes – Normalized or Formed (+N)
    5. DIN 2391‑2 Grade St 30 Si – Normalized or Normalized Formed (N) Steel Tubes for Precision Applications
    6. DIN 1629 Grade St 52.0 – High‑Strength Normalized Steel Tubes
    7. DIN 17175 Grade St 35.8 Tube Steel – Normalized & Normalized Formed (+N) – High‑Temperature Seamless Tubes
    8. DIN 1629 St 37.0 Grade Steel: Normalized or Normalized Formed (+N) – Key Properties & Applications
    9. DIN 1629 Grade St 44.0 Steel – Normalized or Normalized Formed (+N) for Seamless Tubes
    10. DIN 1628 Grade St 37.4 – Normalized & Formed Steel Tubes for High-Performance Engineering