ASTM B241 Grade 5083‑O Aluminum – Up to 20,000 mm²
Additional services: Cuttings, Parts from drawings
ALUDIUM
MANUFACTURER
Information and services
Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, trainingProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | |||
Elongation | 12.0 % | O; Area through 20000 mm2 | ASTM B241 | Tube | |
14.0 % | O; Area through 20000 mm2 | ASTM B241 | Tube | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 270.0 - 350.0 MPa | O; Area through 20000 mm2 | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 - 0.25 % | O; Area through 20000 mm2 | ASTM B241 | Tube |
Copper | 0.1 | O; Area through 20000 mm2 | ASTM B241 | Tube |
Iron | 0.4 | O; Area through 20000 mm2 | ASTM B241 | Tube |
Magnesium | 4.0 - 4.9 % | O; Area through 20000 mm2 | ASTM B241 | Tube |
Manganese | 0.4 - 1.0 % | O; Area through 20000 mm2 | ASTM B241 | Tube |
Silicon | 0.4 | O; Area through 20000 mm2 | ASTM B241 | Tube |
Titanium | 0.15 | O; Area through 20000 mm2 | ASTM B241 | Tube |
Zinc | 0.25 | O; Area through 20000 mm2 | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- ASTM B241 Grade 5454 H111 – 20,000 mm² Tube Area (Aluminium)
- ASTM B241 Grade 5456 H111 Aluminium Tube – 20,000 mm² Cross-Section
- ASTM B241 Grade 5083 H111 Aluminum Plate – Up to 20,000 mm²
- 5083 H112 Aluminium – ASTM B241 Grade for Areas up to 20,000 mm²
- ASTM B241 Grade 5454 H112 Aluminium Tubing – 20,000 mm² Area Specification
- ASTM B241 Grade 5456 Aluminium Tube – 20,000 mm² Area Specification
- ASTM B241 Grade 5454 O – 20,000 mm² Tube Specification
- ASTM B241 Grade 5086 H112 Aluminum: Superior Strength & Corrosion Resistance, Up to 20,000 mm² Area
- ASTM B241 Grade 5086 O Aluminum – Strong, Corrosion‑Resistant Alloy up to 20,000 mm²
- ASTM B241 Grade 5086 H111 Aluminum – High Strength & Corrosion Resistance (≤ 20,000 mm²)