AW-5154A O3 Aluminum – EN 573‑3 Certified Grade for High‑Performance Applications
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.67 g/cm³ | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.5 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.6 GPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire | |
Tensile strength | 210.0 - 250.0 MPa | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.25 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Copper | 0.1 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Iron | 0.50 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Magnesium | 3.1 - 3.9 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Manganese | 0.5 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Silicon | 0.5 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Titanium | 0.2 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Zinc | 0.2 % | O3 | EN 573-3, EN 1715-3, EN 1715-4 | Strip, Sheet, Plate, Rod, Welded Tube, Tube, Wire |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): sufficient - not suitable / sufficient, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good to good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade AW-2014A F Aluminium Alloy – Specifications & Mechanical Properties
- AW-2014A O3 – EN 573-3 Certified Aluminium Grade
- EN 573-3 AW-2014A H18: High-Performance Aluminum Alloy
- EN 573-3 Grade AW-2014A H13 – High-Strength Age-Hardenable AlCu Alloy
- EN 573-3 Grade AW-2024 O3 – High-Strength Aluminum Alloy for Aerospace
- EN 573-3 AW-2024 F Aluminum Alloy – High Strength, Aircraft‑Grade Material
- AW-5154A H16 – High-Strength Aluminum Alloy (EN 573-3)
- EN 573-3 Grade AW-5083 H244 – Aluminium Alloy Properties & Standards
- AW-5083 H114 Aluminum Alloy – EN 573-3 Grade Specification
- EN AW‑2014A T3 Aluminium Alloy – EN 573‑3 Grade Specifications