ASTM B210 Grade 2024 O Aluminum Alloy – High Strength for Aerospace Applications
Aluminum ASTM 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 220.0 | O | ASTM B210 | Seamless Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | O | ASTM B210 | Seamless Tube |
Copper | 3.8 - 4.9 % | O | ASTM B210 | Seamless Tube |
Iron | 0.5 | O | ASTM B210 | Seamless Tube |
Magnesium | 1.2 - 1.8 % | O | ASTM B210 | Seamless Tube |
Manganese | 0.3 - 0.9 % | O | ASTM B210 | Seamless Tube |
Silicon | 0.5 | O | ASTM B210 | Seamless Tube |
Titanium | 0.15 | O | ASTM B210 | Seamless Tube |
Zinc | 0.25 | O | ASTM B210 | Seamless Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B210 Grade 5456-O Aluminium Alloy – Key Properties & Standards
- ASTM B210 Grade 5050-O Aluminum Alloy – Properties & Standards
- ASTM B210 Grade 5154-O Aluminium: Specifications & Properties
- ASTM B316 Grade 2024-O: High‑Strength Aerospace Aluminum Alloy
- ASTM B210 Grade 6262 T9 Aluminum Alloy – High Strength, Corrosion Resistance, & Excellent Machinability
- ASTM B210 Grade 2011 T3 Aluminum Alloy – Superior Machining & Performance
- ASTM B210 Grade 2024 T3 Aluminum – High‑Strength, Aerospace‑Grade Alloy
- ASTM B210 Grade 2024 T42 Aluminum Alloy – High Strength & Machinability for Aerospace Applications
- ASTM B210 Grade 5086O Aluminum: High Strength, Corrosion Resistance & Cost‑Effective Solution
- ASTM B210 Grade 1100O Aluminum – Superior Corrosion Resistance