EN 1652 Grade CuZn39Pb0.5 (R400) – High-Performance Leaded Brass Alloy
Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | -195.0 °C | 108 GPa |
-100.0 °C | 106 GPa | |
20.0 °C | 102 - 105 GPa | |
50.0 °C | 100 GPa | |
100.0 °C | 93 GPa | |
150.0 °C | 91 GPa | |
200.0 °C | 89 GPa | |
250.0 °C | 83 GPa | |
Elongation | 20.0 °C | 20 - 23 % |
Elongation A50 | 20.0 °C | 14 % |
Elongation, transverse | 20.0 °C | 23 % |
Hardness, Vickers | 20.0 °C | 110 [-] |
Shear modulus | 20.0 °C | 37 GPa |
Tensile strength | 20.0 °C | 400 - 480 MPa |
Tensile strength, transverse | 20.0 °C | 400 MPa |
Yield strength Rp0.2 | 20.0 °C | 200 MPa |
50.0 °C | 200 MPa | |
100.0 °C | 190 MPa | |
150.0 °C | 180 MPa | |
Yield strength Rp0.2, transverse | 20.0 °C | 200 - 240 MPa |
50.0 °C | 200 MPa | |
100.0 °C | 190 MPa | |
150.0 °C | 180 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 2.04E-5 1/K | |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 20.0 °C | 109 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.39E+7 S/m |
Electrical resistivity | 20.0 °C | 7.2E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 59 - 60.5 % |
Iron | 0.2 % |
Lead | 0.2 - 0.8 % |
Nickel | 0.3 % |
Tin | 0.2 % |
Metal
- EN 1652 CuCo1Ni1Be TH – High-Performance Copper Alloy for Industrial Applications
- EN 1652 Grade CuZn38Pb2 R400 – Specifications & Properties
- EN 1652 Grade CuZn39Pb0.5 R540 – Unhardenable Wrought Alloy with Enhanced Machinability
- EN 1652 Grade CuSn6 M – Premium Tin-Copper Alloy for Superior Corrosion Resistance
- EN 1652 Grade CuNi2Si M – High-Performance Copper Alloy for Superior Conductivity and Corrosion Resistance
- EN 1652 Grade CuSn5 R400 – Premium Copper‑Tin Alloy for Precision Springs
- EN 1652 Grade CuZn39Pb0.5 R470 – High-Strength Leaded Brass for Cold Forming & Superior Machinability
- EN 1652 CuZn20 (R400) – High-Strength, Unhardenable Wrought Alloy for Jewelry, Automotive & Electronics
- EN 1652 CuZn40 R400 – Premium Copper Alloy for High-Performance Applications
- EN 1652 CuZn39Pb0.5 R340: Unhardenable Wrought Brass Alloy with Enhanced Machinability