ASTM B211 Grade 7075 T651: High-Strength, Low-Weight Aluminum Alloy
ASTM 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.
Additional services: Cuttings, Parts from drawingsSTEEL SCOUT
DISTRIBUTOR
Information and services
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | |||
Tensile strength | 505.0 MPa | T651 | ASTM B211 | Bar, Rod, Wire | |
515.0 MPa | T651 | ASTM B211 | Bar, Rod, Wire | ||
530.0 MPa | T651 | ASTM B211 | Bar, Rod, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.18 - 0.28 % | T651 | ASTM B211 | Bar, Rod, Wire |
Copper | 1.2 - 2.0 % | T651 | ASTM B211 | Bar, Rod, Wire |
Iron | 0.5 | T651 | ASTM B211 | Bar, Rod, Wire |
Magnesium | 2.1 - 2.9 % | T651 | ASTM B211 | Bar, Rod, Wire |
Manganese | 0.3 | T651 | ASTM B211 | Bar, Rod, Wire |
Silicon | 0.4 | T651 | ASTM B211 | Bar, Rod, Wire |
Titanium | 0.2 | T651 | ASTM B211 | Bar, Rod, Wire |
Zinc | 5.1 - 6.1 % | T651 | ASTM B211 | Bar, Rod, Wire |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
Metal
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B210 Grade 7075O Aluminum – Premium High-Strength Aerospace Alloy
- ASTM B211 Grade 7075-O: Premium Aerospace-Grade Aluminum Alloy
- ASTM B211 Grade 2017 Aluminum Alloy – Heat‑Treatable, High Strength & Machinability
- ASTM B241 Grade 7075 O Aluminum: High-Strength Alloy for Aerospace
- ASTM B211 Grade 2011 T3 Aluminum – Exceptional Machining Performance & Strength
- ASTM B211 Grade 2011 Aluminum: T6 & T651 – Performance & Machining Excellence
- ASTM B211 Grade 2011 T8 Aluminum Alloy – Outstanding Machining and Mechanical Performance
- ASTM B211 Grade 3003 O Aluminum – Corrosion‑Resistant & Weldable
- High-Strength ASTM B211 Grade 7075 T6/T62 Aluminum Alloy for Aerospace & Industrial Applications