ASTM B241 Grade 2024 T42 Aluminum Alloy – 16,000–20,000 mm² – High Strength, Good Machinability
Aluminum ASTM 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 7.0 % | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 395.0 MPa | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Copper | 3.8 - 4.9 % | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Iron | 0.5 | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Magnesium | 1.2 - 1.8 % | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Manganese | 0.3 - 0.9 % | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Silicon | 0.5 | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Titanium | 0.15 | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Zinc | 0.25 | T42; Area 16000 - 20000 mm2 | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B241 Grade 5454 H111 – 20,000 mm² Tube Area (Aluminium)
- ASTM B241 Grade 5456 H111 Aluminium Tube – 20,000 mm² Cross-Section
- ASTM B241 Grade 5456 Aluminium Tube – 20,000 mm² Area Specification
- ASTM B241 Grade 5454 O – 20,000 mm² Tube Specification
- ASTM B241 Grade 2014 T62 Aluminum Alloy – 16,000–20,000 mm²: High Strength, Excellent Machinability & Weldability
- ASTM B241 Grade 2024 T42 Aluminum Alloy – 16,000 mm² Area, Aircraft‑Grade Strength & Machinability
- ASTM B241 Grade 2024 T42 Aluminum Alloy – High Strength, Excellent Machinability
- ASTM B241 Grade 5086 H112 Aluminum: Superior Strength & Corrosion Resistance, Up to 20,000 mm² Area
- ASTM B241 Grade 5086 O Aluminum – Strong, Corrosion‑Resistant Alloy up to 20,000 mm²
- ASTM B241 Grade 5086 H111 Aluminum – High Strength & Corrosion Resistance (≤ 20,000 mm²)