ASTM B210 Grade 5005O Aluminum Alloy: Properties & Applications
Aluminum ASTM 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum ASTM 5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum ASTM 5005 is used.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 105.0 - 145.0 MPa | O | ASTM B210 | Seamless Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | O | ASTM B210 | Seamless Tube |
Copper | 0.2 | O | ASTM B210 | Seamless Tube |
Iron | 0.7 | O | ASTM B210 | Seamless Tube |
Magnesium | 0.5 - 1.1 % | O | ASTM B210 | Seamless Tube |
Manganese | 0.2 | O | ASTM B210 | Seamless Tube |
Silicon | 0.3 | O | ASTM B210 | Seamless Tube |
Zinc | 0.25 | O | ASTM B210 | Seamless Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- ASTM B210 Grade 3003 Aluminum Alloy – High Strength & Corrosion Resistance
- ASTM B210 Grade 3003 H12 – Durable, Corrosion‑Resistant Aluminum Alloy
- ASTM B316 Grade 5005 H32 Aluminum Alloy – High Corrosion Resistance & Thermal Conductivity
- ASTM B316 Grade 5005 O – High-Performance Aluminum Alloy for Marine and Industrial Use
- ASTM B210 Grade 7075O Aluminum – Premium High-Strength Aerospace Alloy
- High-Strength ASTM B210 Grade 7075 T6/T62 Aluminum Alloy – Aerospace Grade
- High-Strength ASTM B210 Grade 7075 T73 Aluminum Alloy – Aerospace-Grade Performance
- ASTM B210 Grade 3003 H14 Aluminum: Corrosion-Resistant, Weldable, and Machinable Alloy
- ASTM B210 Grade 3003O Aluminum Alloy – Superior Corrosion Resistance & Weldability
- ASTM B210 Grade 5052-O: Premium Marine-Grade Aluminum Alloy