EN 573-3 Grade 3.0615 T6510 – Comprehensive Technical Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.75 g/cm³ | T6510 | EN 573-3, EN 755 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | T6510 | EN 573-3, EN 755 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 260.0 MPa | T6510 | EN 573-3, EN 755 | |
310.0 MPa | T6510 | EN 573-3, EN 755 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | T6510 | EN 573-3, EN 755 | |
100 °C | 2.3399999999999996e-05 1/K | T6510 | EN 573-3, EN 755 | ||
Melting point | 585.0 - 650.0 °C | T6510 | EN 573-3, EN 755 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 170.0 - 220.0 W/(m·K) | T6510 | EN 573-3, EN 755 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 - 32000000.0 S/m | T6510 | EN 573-3, EN 755 |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m | T6510 | EN 573-3, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuth | 0.7 % | T6510 | EN 573-3, EN 755 |
Chromium | 0.3 % | T6510 | EN 573-3, EN 755 |
Copper | 0.1 % | T6510 | EN 573-3, EN 755 |
Iron | 0.50 % | T6510 | EN 573-3, EN 755 |
Lead | 0.4 - 2.0 % | T6510 | EN 573-3, EN 755 |
Magnesium | 0.6 - 1.2 % | T6510 | EN 573-3, EN 755 |
Manganese | 0.4 - 1.0 % | T6510 | EN 573-3, EN 755 |
Silicon | 0.6 - 1.4 % | T6510 | EN 573-3, EN 755 |
Titanium | 0.2 % | T6510 | EN 573-3, EN 755 |
Zinc | 0.3 % | T6510 | EN 573-3, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Protective: acceptable | |
| Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable | |
| Corrosion properties | Seawater: acceptable, weathering: good | |
| Workability | Bending / Spinning (cold): acceptable / - | |
Metal
- EN 573-3 Grade 3.4345 T6510 Aluminium: Key Properties & Standards
- Grade 3.0615 T6 Aluminum (EN 573‑3) – Key Properties & Standards
- EN 573-3 Grade 3.0615 T6511 – Key Mechanical Properties
- EN 573-3 Grade 3.0615 T4 – Aluminium Properties & Standards
- AW-6026 T6510 – Premium EN 573-3 Grade Aluminum Alloy
- EN 573-3 Grade AW-2014A T6510 – High-Strength Aluminum Alloy for Industrial Applications
- AW-7049A (T6510) – EN 573-3 Grade Aluminum Alloy for Structural Applications
- EN 573-3 Grade 3.4365 T6510 – High‑Strength Aluminum 7075 for Aerospace Applications
- EN 573-3 Grade 3.1255 T6510: High‑Strength, Machinable Aluminum Alloy
- AW-6012 T6510 – High-Strength Age-Hardenable AlMgSi Alloy (EN 573-3 Grade)