EN 573-3 Grade 3.1645 T3510: Technical Specifications of a High-Performance Aluminium Alloy
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.85 g/cm³ | T3510 | EN 573-3, EN 754 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 72.5 GPa | T3510 | EN 573-3, EN 754 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 27.3 GPa | T3510 | EN 573-3, EN 754 | |
Tensile strength | 370.0 MPa | T3510 | EN 573-3, EN 754 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | T3510 | EN 573-3, EN 754 |
100 °C | 2.3e-05 1/K | T3510 | EN 573-3, EN 754 | |
Melting point | 507.0 - 650.0 °C | T3510 | EN 573-3, EN 754 | |
Specific heat capacity | 860.0 J/(kg·K) | T3510 | EN 573-3, EN 754 | |
Thermal conductivity | 130.0 - 160.0 W/(m·K) | T3510 | EN 573-3, EN 754 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 18000000.0 - 22000000.0 S/m | T3510 | EN 573-3, EN 754 |
Electrical resistivity | 4.55e-08 - 5.56e-08 Ω·m | T3510 | EN 573-3, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Bismuth | 0.2 % | T3510 | EN 573-3, EN 754 |
Chromium | 0.1 % | T3510 | EN 573-3, EN 754 |
Copper | 3.3 - 4.6 % | T3510 | EN 573-3, EN 754 |
Iron | 0.80 % | T3510 | EN 573-3, EN 754 |
Magnesium | 0.4 - 1.8 % | T3510 | EN 573-3, EN 754 |
Manganese | 0.1 % | T3510 | EN 573-3, EN 754 |
Nickel | 0.2 % | T3510 | EN 573-3, EN 754 |
Silicon | 0.8 % | T3510 | EN 573-3, EN 754 |
Tin | 0.2 % | T3510 | EN 573-3, EN 754 |
Titanium | 0.2 % | T3510 | EN 573-3, EN 754 |
Zinc | 0.8 % | T3510 | EN 573-3, EN 754 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Protective: poor | |
| Brazing | friction soldering: sufficient | |
| Corrosion properties | Seawater: poor, weathering: poor | |
| Workability | Bending / Spinning (cold): sufficient / -, Deep drawing / upsetting (Condition) - / sufficient | |
Metal
- EN 573-3 Grade 3.1645 Aluminium Alloy – Comprehensive Properties & Standards
- EN 573-3 Grade 3.1325 T3510 – Complete Aluminium Specification & Properties
- EN 573-3 Grade 3.1645 T351 – Comprehensive Material Properties
- EN 573-3 Grade 3.1645 T3511 Aluminium: Key Properties & Standards
- EN 573-3 Grade 3.1645 T4 Aluminium Alloy – Specifications & Mechanical Properties
- EN 573-3 Grade 3.1645 T4510 – Premium Wrought Aluminium Alloy Properties
- EN 573-3 Grade 3.1645 T4511 – Certified Aluminium with Superior Mechanical Properties
- AW-2030 T3510 – Premium Age-Hardenable AlCu Alloy (EN 573-3)
- EN 573-3 Grade 3.1255 T3510: High-Strength Precipitation Hardened Aluminum Alloy
- EN 573-3 Grade 3.1355 T3510 Aluminum Alloy – Aircraft‑Grade Strength & Machinability