AA 7175 T7452 Aluminium Alloy – Standard and Key Properties
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||
Tensile strength | 415.0 MPa | T7452 | AA Standards, ASTM B247 | |
420.0 MPa | T7452 | AA Standards, ASTM B247 | ||
435.0 MPa | T7452 | AA Standards, ASTM B247 | ||
440.0 MPa | T7452 | AA Standards, ASTM B247 | ||
450.0 MPa | T7452 | AA Standards, ASTM B247 | ||
460.0 MPa | T7452 | AA Standards, ASTM B247 | ||
470.0 MPa | T7452 | AA Standards, ASTM B247 | ||
475.0 MPa | T7452 | AA Standards, ASTM B247 | ||
490.0 MPa | T7452 | AA Standards, ASTM B247 | ||
505.0 MPa | T7452 | AA Standards, ASTM B247 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.18 - 0.28 % | T7452 | AA Standards, ASTM B247 |
Copper | 1.2 - 2.0 % | T7452 | AA Standards, ASTM B247 |
Iron | 0.20 % | T7452 | AA Standards, ASTM B247 |
Magnesium | 2.1 - 2.9 % | T7452 | AA Standards, ASTM B247 |
Manganese | 0.1 % | T7452 | AA Standards, ASTM B247 |
Silicon | 0.15 % | T7452 | AA Standards, ASTM B247 |
Titanium | 0.1 % | T7452 | AA Standards, ASTM B247 |
Zinc | 5.1 - 6.1 % | T7452 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): not suitable | |
Metal
- AA 7278A Aluminium Alloy – Technical Specifications
- AA 7349 Aluminium Alloy – Key Mechanical and Thermal Properties
- AA Standard Grade 7449: Comprehensive Mechanical & Thermal Properties
- AA 7095 Aluminium Alloy: Standards & Properties
- AA 7099: Comprehensive Mechanical & Thermal Properties for 7000 Series Aluminium
- AA Standards Grade 7136: Comprehensive Material Properties Overview
- AA Standards Grade 7140 – Key Mechanical & Thermal Properties
- AA Standards Grade 7155 – Comprehensive Material Specifications
- AA Standards Grade 7175 T7454 – Comprehensive Mechanical & Physical Properties
- AA 7050 T7452 – High‑Strength, Heat‑Treatable Aluminium Alloy for Aerospace