EN 573-3 AW-3003 Aluminum Alloy: Superior Corrosion Resistance & Versatile Weldability
Aluminum EN AW-3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, EN AW-3003 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.
Properties
General
| Property | Temperature | Value | Related Standards |
|---|---|---|---|
Density | 20.0 °C | 2.73 g/cm³ | EN 573-3 |
Mechanical
| Property | Temperature | Value | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | -270.0 °C | 70.0 GPa | EN 573-3 | |
20.0 °C | 60.0 - 70.0 GPa | EN 573-3 | ||
20.0 °C | 60.0 - 65.0 GPa | EN 573-3 | ||
20.0 °C | 60.0 - 69.5 GPa | EN 573-3 | ||
20.0 °C | 60.0 - 69.0 GPa | EN 573-3 | ||
20.0 °C | 65.0 - 70.0 GPa | EN 573-3 | ||
20.0 °C | 65.0 - 69.5 GPa | EN 573-3 | ||
20.0 °C | 65.0 - 69.0 GPa | EN 573-3 | ||
20.0 °C | 69.0 GPa | EN 573-3 | ||
20.0 °C | 69.0 - 70.0 GPa | EN 573-3 | ||
20.0 °C | 69.0 - 69.5 GPa | EN 573-3 | ||
20.0 °C | 69.5 - 70.0 GPa | EN 573-3 | ||
20.0 °C | 69.5 GPa | EN 573-3 | ||
20.0 °C | 70.0 GPa | EN 573-3 | ||
50.0 °C | 69.0 GPa | EN 573-3 | ||
100.0 °C | 68.0 GPa | EN 573-3 | ||
150.0 °C | 66.0 GPa | EN 573-3 | ||
200.0 °C | 63.0 GPa | EN 573-3 | ||
250.0 °C | 57.0 GPa | EN 573-3 | ||
300.0 °C | 50.0 GPa | EN 573-3 | ||
Elongation | -196.0 °C | 23.0 - 30.0 % | EN 573-3 | |
-196.0 °C | 23.0 % | EN 573-3 | ||
-196.0 °C | 30.0 % | EN 573-3 | ||
-80.0 °C | 11.0 - 18.0 % | EN 573-3 | ||
-80.0 °C | 11.0 % | EN 573-3 | ||
-80.0 °C | 18.0 % | EN 573-3 | ||
-28.0 °C | 10.0 - 16.0 % | EN 573-3 | ||
-28.0 °C | 10.0 % | EN 573-3 | ||
-28.0 °C | 16.0 % | EN 573-3 | ||
20.0 °C | 10.0 - 16.0 % | EN 573-3 | ||
20.0 °C | 10.0 % | EN 573-3 | ||
20.0 °C | 16.0 % | EN 573-3 | ||
100.0 °C | 10.0 - 16.0 % | EN 573-3 | ||
100.0 °C | 10.0 % | EN 573-3 | ||
100.0 °C | 16.0 % | EN 573-3 | ||
150.0 °C | 11.0 % | EN 573-3 | ||
150.0 °C | 11.0 - 16.0 % | EN 573-3 | ||
150.0 °C | 16.0 % | EN 573-3 | ||
200.0 °C | 18.0 % | EN 573-3 | ||
200.0 °C | 18.0 - 20.0 % | EN 573-3 | ||
200.0 °C | 20.0 % | EN 573-3 | ||
260.0 °C | 60.0 % | EN 573-3 | ||
315.0 °C | 70.0 % | EN 573-3 | ||
370.0 °C | 70.0 % | EN 573-3 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 20.0 °C | 0.33 [-] | EN 573-3 | |
Shear modulus | 20.0 °C | 24.0 - 26.5 GPa | EN 573-3 | |
20.0 °C | 24.0 - 26.1 GPa | EN 573-3 | ||
20.0 °C | 26.1 - 26.5 GPa | EN 573-3 | ||
20.0 °C | 26.1 GPa | EN 573-3 | ||
Tensile strength | -196.0 °C | 240.0 MPa | EN 573-3 | |
-196.0 °C | 240.0 - 280.0 MPa | EN 573-3 | ||
-196.0 °C | 280.0 MPa | EN 573-3 | ||
-80.0 °C | 165.0 MPa | EN 573-3 | ||
-80.0 °C | 165.0 - 220.0 MPa | EN 573-3 | ||
-80.0 °C | 220.0 MPa | EN 573-3 | ||
-28.0 °C | 150.0 MPa | EN 573-3 | ||
-28.0 °C | 150.0 - 205.0 MPa | EN 573-3 | ||
-28.0 °C | 205.0 MPa | EN 573-3 | ||
128.0 MPa | ||||
20.0 °C | 150.0 MPa | EN 573-3 | ||
20.0 °C | 150.0 - 200.0 MPa | EN 573-3 | ||
20.0 °C | 200.0 MPa | EN 573-3 | ||
100.0 °C | 145.0 MPa | EN 573-3 | ||
100.0 °C | 145.0 - 180.0 MPa | EN 573-3 | ||
100.0 °C | 180.0 MPa | EN 573-3 | ||
150.0 °C | 125.0 MPa | EN 573-3 | ||
150.0 °C | 125.0 - 160.0 MPa | EN 573-3 | ||
150.0 °C | 160.0 MPa | EN 573-3 | ||
200.0 °C | 95.0 MPa | EN 573-3 | ||
260.0 °C | 50.0 MPa | EN 573-3 | ||
315.0 °C | 30.0 MPa | EN 573-3 | ||
370.0 °C | 20.0 MPa | EN 573-3 | ||
Yield strength | -196.0 °C | 170.0 MPa | EN 573-3 | RP02 |
-196.0 °C | 170.0 - 230.0 MPa | EN 573-3 | RP02 | |
-196.0 °C | 230.0 MPa | EN 573-3 | RP02 | |
-80.0 °C | 150.0 MPa | EN 573-3 | RP02 | |
-80.0 °C | 150.0 - 200.0 MPa | EN 573-3 | RP02 | |
-80.0 °C | 200.0 MPa | EN 573-3 | RP02 | |
-28.0 °C | 140.0 MPa | EN 573-3 | RP02 | |
-28.0 °C | 140.0 - 190.0 MPa | EN 573-3 | RP02 | |
-28.0 °C | 190.0 MPa | EN 573-3 | RP02 | |
57.0 MPa | ||||
20.0 °C | 140.0 MPa | EN 573-3 | RP02 | |
20.0 °C | 140.0 - 185.0 MPa | EN 573-3 | RP02 | |
20.0 °C | 185.0 MPa | EN 573-3 | RP02 | |
100.0 °C | 130.0 MPa | EN 573-3 | RP02 | |
100.0 °C | 130.0 - 145.0 MPa | EN 573-3 | RP02 | |
100.0 °C | 145.0 MPa | EN 573-3 | RP02 | |
150.0 °C | 110.0 MPa | EN 573-3 | RP02 | |
200.0 °C | 60.0 MPa | EN 573-3 | RP02 | |
260.0 °C | 30.0 MPa | EN 573-3 | RP02 | |
315.0 °C | 15.0 MPa | EN 573-3 | RP02 | |
370.0 °C | 10.0 MPa | EN 573-3 | RP02 |
Thermal
| Property | Temperature | Value | Related Standards | Comment |
|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.15e-05 1/K | EN 573-3 | |
2.33e-05 1/K | ||||
100.0 °C | 2.32e-05 1/K | EN 573-3 | ||
200.0 °C | 2.41e-05 1/K | EN 573-3 | ||
300.0 °C | 2.52e-05 1/K | EN 573-3 | ||
Melting point | 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium | ||
Specific heat capacity | 20.0 °C | 892.0 - 893.0 J/(kg·K) | EN 573-3 | |
20.0 °C | 892.0 J/(kg·K) | EN 573-3 | ||
20.0 °C | 893.0 J/(kg·K) | EN 573-3 | ||
Thermal conductivity | 175.0 W/(m·K) | |||
20.0 °C | 160.0 - 200.0 W/(m·K) | EN 573-3 | ||
20.0 °C | 160.0 W/(m·K) | EN 573-3 |
Electrical
| Property | Temperature | Value | Related Standards |
|---|---|---|---|
Electrical conductivity | 20.0 °C | 22000000.0 - 29000000.0 S/m | EN 573-3 |
20.0 °C | 23000000.0 - 29000000.0 S/m | EN 573-3 | |
Electrical resistivity | 20.0 °C | 3.4e-08 - 4.1e-08 Ω·m | EN 573-3 |
20.0 °C | 3.4e-08 - 4.5e-08 Ω·m | EN 573-3 | |
20.0 °C | 4.1e-08 Ω·m | EN 573-3 | |
20.0 °C | 4.1e-08 - 4.5e-08 Ω·m | EN 573-3 |
Chemical properties
| Property | Value | Related Standards |
|---|---|---|
Copper | 0.05 - 0.2 % | EN 573-3 |
Iron | 0.7 | EN 573-3 |
Manganese | 1.0 - 1.5 % | EN 573-3 |
Silicon | 0.6 | EN 573-3 |
Zinc | 0.1 | EN 573-3 |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- EN AW-3003 Aluminum Alloy – Corrosion-Resistant & Easy Weldability
- EN 573-3 Grade AW-3003 H11: Corrosion-Resistant, Machinable Aluminum Alloy
- EN 573-3 Grade AW-3003 H13: Premium Aluminum Alloy with Superior Corrosion Resistance
- EN 573-3 AW-3003 H15 – Premium Aluminum Alloy for Corrosion Resistance
- EN 573-3 Grade AW-3003 H17: Premium Aluminum Alloy for Superior Corrosion Resistance
- EN 573-3 Grade AW-3003 H224 – Premium Aluminum Alloy with Superior Corrosion Resistance
- EN 573-3 Grade AW-3003 – Premium Aluminum Alloy for Corrosion Resistance & Strength
- EN 573-3: AW-3003 H45 Aluminum Alloy – Durable, Corrosion-Resistant, and Easily Weldable
- EN 573-3 Grade AW-3003 (H49): Premium Aluminum Alloy with Superior Corrosion Resistance
- EN 573-3 AW-3003 Aluminum Alloy – Superior Corrosion Resistance & Workability