EN 573-3 Grade AW-2011 H13 Aluminum Alloy – Superior Machining & Mechanical Performance
Aluminum EN AW-2011 is a popular age-hardenable alloy known for its free-machining characteristics and mechanical properties. It can be machined to very close tolerances while still maintaining a smooth and bright finish. Unlike other aluminum alloys, EN AW-2011 does not offer good corrosion resistance or weldability.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.82 g/cm³ | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
2.83 g/cm³ | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 2.82 g/cm³ | H13 | EN 573-3 | Wire |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
72.5 GPa | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 27.3 GPa | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
Tensile strength | 155.0 - 225.0 MPa | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.14e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire |
-50.0 °C | 2.14e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire | |
20 °C | 2.14e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire | |
20 °C | 2.2899999999999998e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
20 °C | 2.3399999999999996e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
20 °C | 2.4e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire | |
20 °C | 2.4999999999999998e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
100 °C | 2.2899999999999998e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
100.0 °C | 2.29e-05 1/K | H13 | EN 573-3 | Wire | |
100.0 °C | 2.29e-05 - 2.31e-05 1/K | H13 | EN 573-3 | Wire | |
100.0 °C | 2.31e-05 1/K | H13 | EN 573-3 | Wire | |
100 °C | 2.3399999999999996e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
200 °C | 2.4e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire | |
200.0 °C | 2.4e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar, Wire | |
300 °C | 2.4999999999999998e-05 1/K | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
300.0 °C | 2.5e-05 1/K | H13 | EN 573-3 | Wire | |
Melting point | 540.0 - 645.0 °C | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
585.0 - 650.0 °C | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
Specific heat capacity | 864.0 J/(kg·K) | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
20.0 °C | 864.0 J/(kg·K) | H13 | EN 573-3 | Wire | |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
20.0 °C | 151.0 - 172.0 W/(m·K) | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 24000000.0 - 32000000.0 S/m | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
20.0 °C | 23000000.0 - 26000000.0 S/m | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar | |
Electrical resistivity | 3.13e-08 - 4.17e-08 Ω·m | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
3.85e-08 - 4.35e-08 Ω·m | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Bismuth | 0.2 - 0.6 % | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Copper | 5.0 - 6.0 % | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Iron | 0.7 % | H13 | EN 573-3 | Wire |
0.70 % | H13 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
Lead | 0.2 - 0.6 % | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Silicon | 0.4 % | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Zinc | 0.3 % | H13 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not suitable, Protective: poor | |
| Brazing | hard brazing (with flux/ without flux): not suitable /, friction soldering: sufficient | |
| Corrosion properties | Seawater: poor, weathering: sufficient | |
| Workability | Deep drawing / upsetting (Condition) - / acceptable | |
Metal
- EN 573-3 Grade 3.1305 H13 – High Strength Aluminium Alloy
- EN 573-3 Grade AW-1350 H13 Aluminium Alloy – Properties & Standards
- H13 Grade 3.2315 Steel – EN 573-3 Specification
- EN 573-3 Grade 3.1325 H13 – High-Strength Wrought Aluminium Alloy Specifications
- EN 573-3 Grade AW-2011 O3 Aluminum Alloy – Key Properties & Applications
- EN 573-3 AW-2011 F: Premium Age-Hardenable Aluminum Alloy
- EN 573-3 AW-2011 T3: Premium Aluminum Alloy for Precise Machining
- EN 573-3 AW-2011 T4 Aluminum Alloy – High-Performance, Precision Machining
- EN 573-3 Grade AW-2011 T6 – High-Performance Aluminum Alloy
- EN 573-3 AW-2011 T8 Aluminum Alloy – High-Performance Machining & Strength