ASTM B483 Grade 6063 Aluminum – T6 & T62 Finishes for Corrosion-Resistant Construction
Aluminum ASTM 6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, ASTM 6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | |||
Elongation | 10.0 % | T6, T62 | ASTM B483 | Tube | |
12.0 % | T6, T62 | ASTM B483 | Tube | A50 | |
14.0 % | T6, T62 | ASTM B483 | Tube | A50 | |
16.0 % | T6, T62 | ASTM B483 | Tube | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Tensile strength | 230.0 MPa | T6, T62 | ASTM B483 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T6, T62 | ASTM B483 | Tube |
Copper | 0.1 | T6, T62 | ASTM B483 | Tube |
Iron | 0.35 | T6, T62 | ASTM B483 | Tube |
Magnesium | 0.45 - 0.9 % | T6, T62 | ASTM B483 | Tube |
Manganese | 0.1 | T6, T62 | ASTM B483 | Tube |
Silicon | 0.2 - 0.6 % | T6, T62 | ASTM B483 | Tube |
Titanium | 0.1 | T6, T62 | ASTM B483 | Tube |
Zinc | 0.1 | T6, T62 | ASTM B483 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- ASTM B483 Grade 5005 Aluminium: Key Properties & Standards
- ASTM B483 Grade 6063O Aluminum: Premium Architectural Alloy
- ASTM B483 Grade 6063 T83 Aluminum Alloy – Superior Corrosion Resistance & Finishing
- ASTM B483 Grade 6063 T831 Aluminum Alloy – High Corrosion Resistance & Superior Finishing
- ASTM B483 Grade 6063 T832 – Durable, Corrosion‑Resistant Aluminum Alloy
- ASTM B210 Grade 6063 Aluminum – T6 & T4 Temper for Superior Corrosion Resistance
- ASTM B483 Grade 6061 T6/T62 Aluminium Alloy – High Strength & Corrosion Resistance
- ASTM B483 Grade 6063 T4 & T42 Aluminum: Superior Corrosion Resistance & Finishing
- ASTM 6262 Aluminum Alloy – Grade B483, T6/T62 – High Strength, Excellent Machinability
- AA 6063 T62 Aluminum Alloy – High Corrosion Resistance & Superior Finishing