EN 10277-5 Grade Ck22 Cold-Drawn Steel – Ideal for Vehicle and Machine Components

Steel CK 22 is suitable for low strained parts in vehicle manufacturing and machine engineering with higher dimensions (heavy forged parts) and complexer forms as well as higher requirements to uniformity of qualities and surface appearance (e.g. transmission parts, crankshafts). Lowest application temperature -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

5 - 11 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

410 - 580 MPa

Yield strength

20.0 °C

230 - 460 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.17 - 0.24 %

Manganese

0.3 - 0.6 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade 25CrMo4 Cold-Drawn Steel – High Strength & Ductility
    2. EN 10277-5 Grade 25CrMoS4 Cold-Drawn Steel – High Strength & Ductility for Automotive & Industrial Applications
    3. EN 10277-5 Grade 38Cr2 Cold Drawn Steel – High Strength & Low-Temperature Performance
    4. EN 10277-5 Grade 38CrS2 Cold Drawn Steel – Precision Alloy for Automotive and Machinery
    5. EN 10277‑5 Grade 41Cr4 Cold‑Drawn Steel – High‑Performance for Automotive & Machine Engineering
    6. EN 10277-5 Grade 41CrS4 Cold-Drawn Steel – High Strength for Automotive and Industrial Applications
    7. EN 10277-5 Grade 42CrMo4 – Premium Cold‑Drawn Steel for Heavy‑Duty Applications
    8. EN 10277‑5 Grade 46Cr2 Cold‑Drawn Steel – High Strength, Low Ductility for Vehicle Components
    9. EN 10277-5 Grade 46CrS2 Cold Drawn Steel – High Strength & Workability
    10. EN 10277-5 Grade 50CrMo4 Cold Drawn Steel – High‑Strength, Low‑Temperature Performance