ASTM B241 Grade 2024 Aluminum (T3, T3510, T3511) – High Strength & Machinability
Aluminum ASTM 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 9.0 % | T3, T3510, T3511 | ASTM B241 | Tube | |
10.0 % | T3, T3510, T3511 | ASTM B241 | Tube | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 395.0 MPa | T3, T3510, T3511 | ASTM B241 | Tube | |
415.0 MPa | T3, T3510, T3511 | ASTM B241 | Tube | ||
450.0 MPa | T3, T3510, T3511 | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T3, T3510, T3511 | ASTM B241 | Tube |
Copper | 3.8 - 4.9 % | T3, T3510, T3511 | ASTM B241 | Tube |
Iron | 0.5 | T3, T3510, T3511 | ASTM B241 | Tube |
Magnesium | 1.2 - 1.8 % | T3, T3510, T3511 | ASTM B241 | Tube |
Manganese | 0.3 - 0.9 % | T3, T3510, T3511 | ASTM B241 | Tube |
Silicon | 0.5 | T3, T3510, T3511 | ASTM B241 | Tube |
Titanium | 0.15 | T3, T3510, T3511 | ASTM B241 | Tube |
Zinc | 0.25 | T3, T3510, T3511 | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B211 Grade 2024 O Aluminum – Superior Strength for Aerospace
- ASTM B211 Grade 2024 T351 Aluminum Alloy – High Strength, Aircraft-Grade Material
- ASTM B211 Grade 2024 T851 Aluminum Alloy – High Strength, Aircraft Grade
- ASTM B241 Grade 2024-O Aluminum Alloy – Superior Strength for Aerospace Applications
- ASTM B241 Grade 2024 T42 Aluminum Alloy – High Strength, Excellent Machinability
- ASTM B316 Grade 2024 T42 Aluminum Alloy – High Strength for Aircraft Applications
- ASTM B211 2024‑T4 Aluminum Alloy – High Strength for Aerospace Applications
- ASTM B211 Grade 2024 T42 Aluminum Alloy – High Strength & Machinability
- ASTM B211 Grade 2024 T6 Aluminum: High-Strength, Aircraft-Grade Alloy
- ASTM B241 Grade 2024 Aluminum Alloys: T81, T8510, T8511 – High Strength & Machinability