EN 573-3 Grade 3.0525 H111 – High-Quality Aluminum Alloy for Industrial Applications
Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.72 g/cm³ | H111 | EN 573-3, EN 485 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 1.0 °/t | H111 | EN 573-3, EN 485 | |
Bending angle 90° | 0.5 °/t | H111 | EN 573-3, EN 485 | |
1.0 °/t | H111 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa | H111 | EN 573-3, EN 485 | |
Hardness, Brinell | 33.0 [-] | H111 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Tensile strength | 115.0 - 165.0 MPa | H111 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3199999999999998e-05 1/K | H111 | EN 573-3, EN 485 | |
100 °C | 2.3199999999999998e-05 1/K | H111 | EN 573-3, EN 485 | ||
Melting point | 630.0 - 654.0 °C | H111 | EN 573-3, EN 485 | ||
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
Thermal conductivity | 160.0 - 190.0 W/(m·K) | H111 | EN 573-3, EN 485 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 23000000.0 - 25000000.0 S/m | H111 | EN 573-3, EN 485 |
Electrical resistivity | 4e-08 - 4.35e-08 Ω·m | H111 | EN 573-3, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % | H111 | EN 573-3, EN 485 |
Copper | 0.3 % | H111 | EN 573-3, EN 485 |
Iron | 0.70 % | H111 | EN 573-3, EN 485 |
Magnesium | 0.2 - 0.6 % | H111 | EN 573-3, EN 485 |
Manganese | 1.0 - 1.5 % | H111 | EN 573-3, EN 485 |
Silicon | 0.6 % | H111 | EN 573-3, EN 485 |
Titanium | 0.1 % | H111 | EN 573-3, EN 485 |
Zinc | 0.25 % | H111 | EN 573-3, EN 485 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: very good | |
| Corrosion properties | Seawater: very good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (O) / acceptable (H12) | |
Metal
- EN 573-3 Grade 3.0915 (H111) – Premium Aluminium Alloy
- EN 573-3 Grade 3.0525 F – Wrought 3000 Series Aluminium Properties
- EN 573-3 Grade 3.3326 H111 – Detailed Mechanical Properties of 5000 Series Aluminium
- EN 573-3 Grade 3.0525 H41 – Aluminum Alloy Specification & Key Properties
- EN 573-3 Grade 3.0525 H42 – High‑Strength Aluminium Alloy Specification
- EN 573-3 Grade 3.0525 H44 – High-Quality Aluminium Standard Specifications
- EN 573-3 Grade 3.0525 H45 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.0525 H46 Aluminium Alloy – Properties & Standards
- EN 573-3 Grade 3.0525 H48 – Comprehensive Aluminum Alloy Specifications
- EN 573-3 Grade 3.0505 H111 Aluminium Alloy - Technical Specifications