AW-6101B T7 Aluminum Grade per EN 573-3
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.69 g/cm³ | T7 | EN 573-3, EN 755 | Rod, Tube |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | T7 | EN 573-3, EN 755 | Rod, Tube | |
Hardness, Brinell | 55.0 [-] | T7 | EN 573-3, EN 755 | Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Tensile strength | 170.0 MPa | T7 | EN 573-3, EN 755 | Rod, Tube |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | T7 | EN 573-3, EN 755 | Rod, Tube | |
100 °C | 2.35e-05 1/K | T7 | EN 573-3, EN 755 | Rod, Tube | ||
Melting point | 620.0 - 655.0 °C | T7 | EN 573-3, EN 755 | Rod, Tube | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | ||||
Thermal conductivity | 218 W/(m·K) | T7 | EN 573-3, EN 755 | Rod, Tube |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 33000000.0 S/m | T7 | EN 573-3, EN 755 | Rod, Tube |
Electrical resistivity | 3.03e-08 Ω·m | T7 | EN 573-3, EN 755 | Rod, Tube |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Copper | 0.05 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Iron | 0.1 - 0.3 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Magnesium | 0.35 - 0.6 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Manganese | 0.05 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Silicon | 0.3 - 0.6 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Zinc | 0.1 % | T7 | EN 573-3, EN 755 | Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good to acceptable / good, friction soldering: very good, soft brazing with flux: very good | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / -, Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |
Metal
- EN 573-3 Grade 3.0505 F Aluminium Alloy: Properties & Standards
- EN 573-3 Grade 3.1305 F Aluminium Alloy – Key Mechanical Properties
- EN 573-3 Grade 3.1305 O Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.1305 O3 – Comprehensive Aluminium Alloy Specifications
- EN 573-3 Grade 3.3316 F – Key Properties & Standards for 5000 Series Aluminium
- EN 573-3 Grade 3.3549 F – Premium Aluminum Alloy with Expert R&D Support
- EN 573-3 AW‑1090 F Aluminium: Technical Specifications & Standards
- AW-5356 F Aluminum Alloy – EN 573‑3 Specification & Key Mechanical Properties
- EN 573-3 Grade AW-5356 O3 Aluminium Alloy – Key Properties & Standards
- EN 573-3 AW‑6101B T6: Premium Age-Hardenable AlMgSi Alloy