BS EN 573-3: Grade 3103 H14 Aluminium - Technical Specifications
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.73 g/cm³ | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
2.8 g/cm³ | H14 |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.5 GPa | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
72.0 GPa | H14 | ||||
Elongation | 4.6 % | H14 | |||
Hardness, Brinell | 45.0 [-] | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Tensile strength | 140.0 - 180.0 MPa | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
150.0 MPa | H14 | ||||
Yield strength | 130.0 MPa | H14 |
Thermal
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K | H14 | ||
2.31e-05 1/K | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Melting point | 640.0 °C | H14 | ||
655.0 °C | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Specific heat capacity | 890.0 J/(kg·K) | H14 | ||
Thermal conductivity | 160.0 W/(m·K) | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
Electrical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium | |||
Electrical resistivity | 4.11e-08 Ω·m | H14 | BS EN 573-3, BS EN 485-2 | Sheet |
Chemical properties
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Aluminium | 96.3 - 99.1 % | H14 | |||
Chromium | 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Copper | 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Iron | 0.7 % | H14 | |||
Magnesium | 0.3 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Manganese | 0.9 - 1.5 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Other | 0.15 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | Total |
Silicon | 0.5 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Titanium | 0.1 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | Ti + Zr |
Zinc | 0.2 % | H14 | BS EN 573-3, BS EN 485-2 | Sheet | |
Zirconium | 0.1 % | H14 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Very Good | |
| General machinability | Acceptable | |
| Soldering general | Very Good | |
| Welding | Gas: Very Good; Arc: Very Good; Resistance: Good | |
| Workability | Cold: Good | |
Metal
- EN 573-3 Grade 3.3316 H14 Steel – Comprehensive Properties & Standards
- EN 573-3 Grade AW-1350 H14 – Steel Properties & Standards
- EN 573-3 AW-1100 H14: Pure, Corrosion-Resistant Aluminum Alloy
- EN 573-3 Grade 3.3555 H14 Aluminium: Properties & Standards
- EN 573-3 Grade 3.3537 H14 Aluminium Alloy – Specifications & Properties
- EN 573-3 Grade 3.3547 H14 – Key Properties & Standards
- AW-1098 H14 Aluminum – EN 573-3 Certified Food‑Safe Grade
- EN 573-3 Grade AW-6063 H14 – Premium Architectural Aluminum Alloy with Superior Corrosion Resistance
- AW-4006 H14 Aluminum Alloy – EN 573-3 Certified Food‑Safe Grade
- AW‑5051A H14 AlMg Alloy: Food‑Safe, High‑Performance EN 573‑3 Grade