Alloy 165 (C17000) TB00 Tube – High Strength & Fatigue Resistance
Alloy 165 Tube from Materion Brush Performance Alloys provides strength close to that of Alloy 25, with slightly lower beryllium content. Alloy 165 features high fatigue strength and magnetic permeability approaching unity.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.41 g/cm³ |
Dimension
| Property | Value |
|---|---|
Outside diameter | 19.1 - 406 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 131 GPa |
Elongation | 23.0 °C | 20 - 60 % |
Tensile strength | 23.0 °C | 410 - 590 MPa |
Yield strength Rp0.2 | 23.0 °C | 130 - 250 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K |
Melting point | 870 °C | |
Thermal conductivity | 23.0 °C | 105 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 5.8E-6 - 6.9E-6 Ω·m |
Specific Electrical conductivity | 25 - 30 % IACS |
Magnetic
| Property | Temperature | Value | Comment |
|---|---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] | max. |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Beryllium | 1.6 - 1.85 % | ||
Cobalt | 0.2 % | min. Nickel + Cobalt | |
Copper | Balance | ||
Iron | 0.6 % | max., Nickel + Cobalt + Iron | |
Nickel | 0.2 % | min. Nickel + Cobalt | |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Alloy 165 tube is used in crucial telecommunications applications including undersea instrument housings and repeater housings. | |
Metal
- Alloy 165 – Premium High‑Strength Material for Forging & Extrusion (C17000)
- Alloy 165 (C17000) TB00 Rods & Bars – High Strength, Low Beryllium, Industrial-Grade Performance
- Alloy 3 (C17510) TB00 Tube – Superior Electrical & Thermal Performance
- Alloy 10 (C17500) TB00 Tube – High Conductivity, Reliable Performance
- High-Strength Alloy 165 (C17000) TH04 Plate – Superior Fatigue & Corrosion Resistance
- Alloy 165 Plate – High Strength, Wear-Resistant TB00 Material
- Alloy 165 (C17000) TD04 Plate – High‑Strength, Wear‑Resistant Performance Alloy
- Alloy 165 (C17000) TD04 Tube – High Fatigue Strength & Low Beryllium for Peak Performance
- Alloy 165 (C17000) TF00 Tube – High Strength, Low Beryllium, Near‑Unity Magnetic Permeability
- Alloy 165 TH04 Tube – High Strength, Low Beryllium Alloy