AA 6463 T1 Aluminium Standard – Key Properties & Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.69 g/cm³ | T1 | AA Standards, ASTM B221 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 70.0 MPa | T1 | AA Standards | |
Elastic modulus | 69.0 GPa | T1 | AA Standards, ASTM B221 | |
Hardness, Brinell | 42.0 [-] | T1 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Tensile strength | 115.0 MPa | T1 | AA Standards, ASTM B221 | |
150.0 MPa | T1 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221 | |
100 °C | 2.3399999999999996e-05 1/K | T1 | AA Standards, ASTM B221 | ||
Melting point | 615.0 - 655.0 °C | T1 | AA Standards, ASTM B221 | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Thermal conductivity | 193.0 - 209.0 W/(m·K) | T1 | AA Standards, ASTM B221 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 29000000.0 - 32000000.0 S/m | T1 | AA Standards, ASTM B221 |
Electrical resistivity | 3.13e-08 - 3.45e-08 Ω·m | T1 | AA Standards, ASTM B221 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Copper | 0.2 % | T1 | AA Standards, ASTM B221 |
Iron | 0.15 % | T1 | AA Standards, ASTM B221 |
Magnesium | 0.45 - 0.9 % | T1 | AA Standards, ASTM B221 |
Manganese | 0.05 % | T1 | AA Standards, ASTM B221 |
Silicon | 0.2 - 0.6 % | T1 | AA Standards, ASTM B221 |
Zinc | 0.05 % | T1 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (T1), sufficient (T5, T6) | |
| Workability | general (condition): acceptable (T1, T5), poor(T6) | |
Metal
- AA Standards Grade 7122 – Aluminium Alloy Specifications & Properties
- AA 7068 Aluminium Alloy Standard – Key Properties & Specifications
- AA Standards Grade 3105A – Key Mechanical & Thermal Properties
- AA 2041 Aluminium Standard – Mechanical & Thermal Properties
- AA Standards Grade 2044 – Detailed Mechanical & Thermal Properties
- AA 6560 T5 Aluminum Alloy: Comprehensive Standards & Mechanical Properties
- AA 6560 T6 Aluminium Alloy: Key Mechanical Properties & Standards
- AA Standards Grade 6463 T62 – Key Mechanical Properties & Specifications
- AA Standards Grade 6463 T5 – Comprehensive Mechanical Properties & Standards
- AA 6463 T6 Aluminium: Standard Mechanical Properties & Specifications