ASTM B211 Grade 1100 O Aluminum Alloy – High Corrosion Resistance & Purity
ASTM 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, ASTM 1100 is purest grade of aluminum alloy available commercially.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 1000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 68.0 - 70.0 GPa | Typical for Wrought 1000 Series Aluminium | |||
Elongation | 22.0 % | O | ASTM B211 | Bar, Rod, Wire | |
25.0 % | O | ASTM B211 | Bar, Rod, Wire | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | |||
Tensile strength | 75.0 - 105.0 MPa | O | ASTM B211 | Bar, Rod, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 1000 Series Aluminium |
Melting point | 645.0 - 660.0 °C | Typical for Wrought 1000 Series Aluminium |
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium |
Thermal conductivity | 167.0 - 244.0 W/(m·K) | Typical for Wrought 1000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 33000000.0 - 38000000.0 S/m | Typical for Wrought 1000 Series Aluminium |
Electrical resistivity | 2.7e-08 - 3e-08 Ω·m | Typical for Wrought 1000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 99.0 % | O | ASTM B211 | Bar, Rod, Wire |
Copper | 0.05 - 0.2 % | O | ASTM B211 | Bar, Rod, Wire |
Manganese | 0.05 | O | ASTM B211 | Bar, Rod, Wire |
Zinc | 0.1 | O | ASTM B211 | Bar, Rod, Wire |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Workability | Excellent workability. | |
Metal
- ASTM B211 Grade 1100 H16 Aluminum – High Corrosion Resistance & Purest 1000 Series Alloy
- ASTM B211 Grade 1100 H18 Aluminum – 99% Pure, Corrosion-Resistant & Lightweight
- ASTM B316 Grade 1100 O Aluminum Alloy – Superior Corrosion Resistance & Purest 1000 Series
- ASTM B211 Grade 1100 H14 Aluminum: Superior Corrosion Resistance & High Purity
- ASTM B211 Grade 1100 H12 – Premium 99% Aluminum Alloy with Superior Corrosion Resistance
- ASTM B483 Grade 1100 O Aluminum: Pure, Corrosion-Resistant, Low-Strength Alloy
- ASTM B210 Grade 1100O Aluminum – Superior Corrosion Resistance
- ASTM B211 Grade 6262 (T8) – High-Performance Aluminum Alloy for Machining & Corrosion Resistance
- ASTM B211 Grade 6262 T9: High-Strength, Corrosion-Resistant Aluminum Alloy
- ASTM B241 Grade 1100 O Aluminum – Superior Corrosion Resistance & Low‑Strength Alloy