EN 573-3 Grade AW-6065 T9 Aluminium Alloy – Technical Specifications
Age-hardenable AlMgSi alloy. The alloy is not food safe.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.72 g/cm³ | T9 | EN 573-3, EN 754 | Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Elongation | 3.0 % | T9 | EN 573-3, EN 754 | Rod, Tube | A50 | |
4.0 % | T9 | EN 573-3, EN 754 | Rod, Tube | A100 | ||
20.0 °C | 3.0 % | T9 | EN 573-3 | Rod | A50 | |
20.0 °C | 4.0 % | T9 | EN 573-3 | Rod | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Tensile strength | 360.0 MPa | T9 | EN 573-3, EN 754 | Rod, Tube | ||
20.0 °C | 360.0 MPa | T9 | EN 573-3 | Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Bismuth | 0.5 - 1.5 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Chromium | 0.15 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Copper | 0.15 - 0.4 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Iron | 0.7 % | T9 | EN 573-3 | Rod |
0.70 % | T9 | EN 573-3, EN 754 | Rod, Tube | |
Lead | 0.05 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Magnesium | 0.8 - 1.2 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Manganese | 0.15 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Silicon | 0.4 - 0.8 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Titanium | 0.1 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Zinc | 0.25 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Zirconium | 0.15 % | T9 | EN 573-3, EN 754 | Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- EN 573-3 AW-8008 O – Food‑Safe, High‑Strength AlFeMn Alloy
- AW-4007 F Aluminum Alloy – EN 573-3 Certified, Food-Safe, High-Strength
- AW‑6951 O (EN 573‑3): Food‑Safe Age‑Hardenable AlMgSi Alloy
- AW-5040 O: Certified Food‑Safe Aluminium Alloy (EN 573‑3)
- AW-2618A T6 – Premium Age-Hardenable AlCu Alloy (EN 573-3 Grade)
- AW-6064A T8 Aluminium Alloy – EN 573-3 Certified Grade
- AW-6064A T9: EN 573-3 Certified Age-Hardenable AlMgSi Alloy
- AW‑6065 T6 Aluminium Alloy – EN 573‑3 Certified
- EN 573-3 Grade AW-6065 T8 Aluminum Alloy – Technical Specs & Properties
- AW-6261 O Alloy: EN 573-3 Grade, Food‑Safe, Age‑Hardenable Aluminium